Abstract:The incompatibility between inorganic flame retardants and organic acrylic coatings represents a significant challenge that requires resolution. This work selected environmentally friendly organic aqueous acrylic coatings as the substrate, sodium silicate hydrate as the inorganic flame retardant, and melamine cyanurate (MCA) as the flame-retardant modifier and the flame-retardant co-modifier, with the objective of improving the dispersion and flame-retardant properties of sodium silicate hydrate in the aqueous acrylic coatings. Subsequently, the sodium silicate/MCA/waterborne acrylic acid flame-retardant coating was prepared. The flame-retardant treatment was then applied to poplar veneer in order to create a flame-retardant poplar veneer. The dispersion of the flame-retardant coating was characterized by scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDX), and X-ray diffractometry (XRD). Furthermore, the flame-retardant properties of the flame-retardant poplar veneer were analyzed by thermogravimetry (TG), limiting oxygen index (LOI), and cone calorimeter. The results demonstrated that the MCA-modified sodium silicate flame retardant was well dispersed in aqueous acrylic coatings. The results of the flame-retardant properties of the poplar veneer indicated that the ignition time of the 9% flame retardant-treated poplar veneer was increased by 122.7%, the limiting oxygen index value was increased by 43.0%, and the peak heat release rate (pHRR), the peak total heat release rate (pTHR), and the peak mass loss rate were decreased by 19.9%, 10.8%, and 27.2%, respectively, in comparison to the non-flame retardant-treated poplar veneer. Furthermore, the residual char mass increased by 14.4%, and the residual char exhibited enhanced thickness, density, and regularity. The results demonstrated that MCA was an effective promoter of sodium silicate dispersion in acrylic coatings. Furthermore, the sodium silicate/MCA/waterborne acrylic flame-retardant coating significantly enhance the flame retardancy of wood, and its flame retardant mechanism was consistent with the synergistic silicone–nitrogen expansion flame-retardant mechanism. This work presents a novel approach to enhancing the dispersion of inorganic flame retardants in organic coatings, offering a valuable contribution to the advancement of research and application in the domains of innovative flame retardant coatings and flame retardant wood.

Synergistic flame retardant effect of a new N-P flame retardant on poplar wood density board

A novel cysteine-based flame retardant for biomass poplar wood density board

Flame retardant modification of poplar wood based on sustainable impregnation solution with high biomass content

Flame-retardant smoke-suppressing and antibacterial poplar wood enabled by a bio-based flame retardant containing transition metal

Phytic acid-based NP fire retardant and its effect on combustion property of poplar wood

Synthesis of fire retardants based on N and P and poly(sodium silicate-aluminum dihydrogen phosphate) (PSADP) and testing the flame-retardant properties of PSADP impregnated poplar wood

Preparation of Organic-Inorganic Phosphorus-Nitrogen-Based Flame Retardants and Their Application to Plywood

Effect of Modification on Mechanical Property and Fire-Retardant Behavior of Fast-Growing Poplar Wood

Flame Retardancy of Densified Wood Modified by Bio-Material Based Flame Retardant

Montmorillonite-Synergized Water-Based Intumescent Flame Retardant Coating for Plywood

Preparation of multifunctional flame retardant composite wood by doping poplar cell walls with metal phytates

A Novel Halogen‐free Intumescent Flame Retardant Containing Phosphorus and Nitrogen and Its Application in Polypropylene Systems

Preparation of highly-densified modified poplar wood by evacuating the micro-pores of wood through a gas expansion method

Combustion Behavior and Thermal Degradation Properties of Wood Impregnated with Intumescent Biomass Flame Retardants: Phytic Acid, Hydrolyzed Collagen, and Glycerol

Enhancing wood stability and fire retardancy through citric acid and phosphorylated sucrose stearate cross-linking modification

A highly efficient, colorless phosphorus–nitrogen synergistic flame retardant for durable flame retardancy in wood pulp paper

A Novel Intumescent MCA-Modified Sodium Silicate/Acrylic Flame-Retardant Coating to Improve the Flame Retardancy of Wood

In Situ Polymerization and Flame Retardant Mechanism of Bio-Based Nitrogen and Phosphorus Macromolecular Flame Retardant in Plywood

A novel biobased intumescent flame retardant through combining simultaneously char-promoter and radical-scavenger for the application in epoxy resin

Analyzing Temperature Distribution Patterns on the Facing and Backside Surface: Investigating Combustion Performance of Flame-Retardant Particle Boards Using Aluminum Hypophosphite, Intumescent, and Magnesium Hydroxide Flame Retardants

A flame-retardant densified wood as robust and fire-safe structural material