Abstract:This research has demonstrated that SiO 2 impregnation under high vacuum pressure of − 90 kPa can significantly reduce porosity by almost 10%, and improve the mechanical and viscoelastic properties of spruce wood under dry and saturated states. Characterization methods, such as impact test, DMA, SEM, EDS, porosity and SAXS tests were conducted on non-treated and − 90 kPa treated spruce wood samples under dry, saturated and submerged states to analyze the synergistic effect of high vacuum SiO 2 impregnation pressure on wood properties. The results showed that high vacuum impregnation pressure had a significant positive reinforcing effect on wood's properties. It increased the impact resistance of wood under dry and saturated conditions. Additionally, the high vacuum impregnation technique was able to overcome the water-induced softening effect and caused a significant increase in the storage modulus through uniform dispersion of the SiO 2 particles in the wood's vascular structure. Consequently, the impregnation reinforced the wood and ameliorated its capacity to absorb energy. High vacuum impregnation was also able to counteract the plasticizing effect of the water molecules and significantly increased the loss modulus by increasing the internal friction and cohesion of the wood components with the addition of the nanoparticles to the vascular system, which increased the wood's capacity to transform and dissipate energy. Quantitatively and qualitatively, impregnation under a vacuum pressure of − 90 kPa exhibited an effective obstruction of the vascular structure of spruce wood. In all conditions, high vacuum-impregnated samples showed significant enhancements over non-treated samples. This research demonstrated that high vacuum SiO 2 impregnation is an effective wood processing technique. Multiple materials and applications could benefit from this research wherein high strain-rate deformations are expected to occur or when simultaneous elastic behaviour of wood and its damping energy is needed. This study could also pave the way for research on the synergistic effect of SiO 2 impregnation and water absorption on the viscoelastic behaviour of wood.

Preparation of highly-densified modified poplar wood by evacuating the micro-pores of wood through a gas expansion method

High-pressure Densification and Hydrophobic Coating for Enhancing the Mechanical Properties and Dimensional Stability of Soft Poplar Wood Boards

Effects of High-Pressure Treatment on Poplar Wood: Density Profile, Mechanical Properties, Strength Potential Index, and Microstructure

Plastic and Elastic Strains in Poplar Wood under High-Pressure Densification

Building bridging structures and crystallization reinforcement in sodium silicate-modified poplar by dimethylol dihydroxyethylene urea

Development of super dimensional stable poplar structure with fire and mildew resistance by delignification/densification of wood with highly aligned cellulose molecules

Integrated approach for improving mechanical and high-temperature properties of fast-growing poplar wood using lignin-controlled treatment combined with densification

Preparation and properties of modified poplar impregnated with PVA-nano silica sol composite dispersion system

Research on the Impregnation Process and Mechanism of Silica Sol/Phenolic Resin Modified Poplar Wood

Study on Poplar Densification by Cross-Grain Compression

Preparation Optimization of Enhanced Poplar Wood by Organic–Inorganic Hybrid Treatment via Response Surface Methodology

The study of physico-mechanical properties of SiO2-impregnated wood under dry and saturated conditions

Characterization of Microstructure, Chemical, and Physical Properties of Delignified and Densified Poplar Wood

Flame retardant modification of poplar wood based on sustainable impregnation solution with high biomass content

Chemical modification of poplar wood featuring compressible rebound 3D structure as water treatment absorbents

Study on the Effect of Acrylic Acid Emulsion on the Properties of Poplar Wood Modified by Sodium Silicate Impregnation

Effect of Modification on Mechanical Property and Fire-Retardant Behavior of Fast-Growing Poplar Wood

Developing poplar wood into a green structure-decoration integrated material for prefabricated wooden building application

Effects of High-Temperature Heat Treatment Modification by Impregnation on Physical and Mechanical Properties of Poplar

Effective strategy for fabricating surface impregnated and unilaterally densified wood with furfuryl alcohol/flame retardants for enhanced mechanical performance and flame retardancy

Organic–inorganic hybrid material containing silica–alumina sol and ether polymer for flame retardant wood with decay resistance and excellent mechanical properties