Abstract:In this study, the effect of Sc content on the microstructural characteristics and phase evolution of an Al–Cu–Li alloy under as-cast and homogenization conditions was investigated. The results show the grain refinement effect was distinct when the content of Sc was 0.16 wt%. However, further increased in Sc content resulted in a limited decrease in grain size. Besides, In the 0.16Sc alloy, the flocculent phase with primary Al 3 (Sc,Zr) phase coexisting with W (Al 8-x Cu 4+x Sc) phase appeared, and in the 0.32Sc alloy, the additional blocky primary Al 3 (Sc,Zr) phase was observed. With the increased of Sc content, the proportion of primary Al 3 (Sc,Zr) and W phases gradually increased, and the number and size of Al 2 Cu and Ag-containing Al 2 CuMg phases at grain boundaries gradually decreased. Two different morphologies of the primary W phase, flocculent and long strip shaped, were revealed within the Sc-containing alloy. The formation of the core-shell structure formed by Al 3 (Sc,Zr) particles and W phase was generated by the peritectic-eutectic reaction (Liquid + Al 3 (Sc,Zr)→α-Al + W) and the long strip of W phase was generated by the eutectic reaction (Liquid→α-Al + Al 2 Cu + W). During the homogenization process, the Al 2 Cu and Ag-containing Al 2 CuMg phases were completely re-dissolved after the two previous stages of homogenization, and only a small amount of the spheroidal residual W phase persisted. A subsequent low temperature treatment was employed to allow the Sc atoms that had diffused into the Al matrix to precipitate as Al 3 (Sc,Zr) dispersoids, resulting in a higher number density of Al 3 (Sc,Zr) particles for more efficiently utilizing the Sc elements.

Effect of grain structures and precipitation characteristics on the corrosion behaviour of Sc-containing Al-Cu-Li alloy

Effect of aging on the mechanical properties and corrosion susceptibility of an Al-Cu-Li-Zr alloy containing Sc

Corrosion behavior of Al-6.8Zn-2.2Mg-Sc-Zr alloy with high resistance to intergranular corrosion

Effect of minor Sc additions on precipitation and mechanical properties of a new Al-Cu-Li alloy under T8 temper

Investigation on the microstructural evolution and corrosion behaviors of Zn-microalloyed Al-Cu-Li alloys

EFFECT OF Sc ON MICROSTRUCTURE AND PROPERTIES OF Al-Li-Cu-Mg-Zr ALLOY

Microstructures evolution and mechanical properties disparity in 2070 Al-Li alloy with minor Sc addition

Effect of Sc content on microstructure characteristics and evolution of W phase in Al–Cu–Li alloys under as-cast and homogenization conditions

Role of intermetallic phases in initiation and propagation of intergranular corrosion of an Al-Li-Cu-Mg alloy

Enhancing the strength of Sc-containing Al-Cu-Li alloys by modifying the precipitation behavior through plastic deformation and heat treatment

Tailoring the corrosion behavior and mechanism of Mg-Gd-Zn alloys via Sc microalloying

Effect of quenching protocols on microstructure and corrosion morphology in a recycled Al–Mg–Si alloy: Tracing Cu impurities

Precipitate microstructures, mechanical properties and corrosion resistance of Al-1.0 wt%Cu-2.5 wt%Li alloys with different micro-alloyed elements addition

Phase-field investigation of intergranular corrosion mechanism and kinetics in aluminum alloys

Competition between precipitation and segregation of Sc and its effects on thermal stability of Al-Cu-Mg-Ag alloys

Effect of creep ageing on the corrosion behaviour of an Al–Cu–Li alloy

Effect of crystal orientations and precipitates on the corrosion behavior of the Al-Cu alloy using single crystals

Effects of grain boundary chemistry and precipitate structure on intergranular corrosion in Al-Mg-Si alloys doped with Cu and Zn

Discontinuous Precipitation of Nano-Al3Sc Particles in Al-Sc Alloy and Its Effect on Mechanical Property

Influence of grain structure and precipitates on fatigue crack propagation behaviors of Al- x Cu-1.2Li-X alloys

Microstructure and corrosion behavior of as-homogenized and as-extruded Mg−xLi−3Al−2Zn−0.5Y alloys (x=4, 8, 12)