Abstract:Calcium silicate cement has attracted much attention for bone defect repair and regeneration due to its osteogenic properties. Biomaterial-associated infections and washout have become a common clinical problem. In order to enhance the antibacterial and washout performance of calcium silicate cement to meet clinical needs, different types of chitosan, including chitosan polysaccharide (CTS), quaternary ammonium chitosan (QTS), and chitosan oligosaccharide (COS), as a liquid phase were added to the calcium silicate powder. The physicochemical properties, in vitro bioactivity, antibacterial efficacy, and osteogenic effects (MG63 cells) of the cement were evaluated. Antibacterial activity was conducted with Gram-negative Escherichia coli (E. coli) and a Gram-positive Staphylococcus aureus (S. aureus) bacteria. The amount of intracellular reactive oxygen species (ROS) produced in the bacteria cultured with the chitosan solution was also detected. The experimental results showed that the chitosan additive did not affect the crystalline phase of calcium silicate cement, but increased the setting time and strength of the cement in a concentration-dependent manner. Within the scope of this study, CTS and QTS solutions with a concentration of not <1 wt% improved the washout resistance of the control cement, while the COS solutions failed to strengthen the cement. When soaked in simulated body fluid (SBF) for 1 day, all cement samples formed apatite spherules. As the soaking time increased, the diametral tensile strength of all cements decreased and the porosity increased. The assays of MG63 cell function showed lower osteogenic activity of osteoblastic cells grown on the surfaces of the chitosan-incorporated cements in comparison with the control cement without chitosan. At the same 1% concentration, compared with QTS and COS cement, CTS cement had lower cell attachment, proliferation, differentiation, and mineralization. Conversely, the CTS cement resulted in the highest bacteriostasis ratio among the three hybrid cements against two bacteria. The ROS production followed the order of CTS > QTS > COS at the same 1% concentration. In conclusion, calcium silicate cement with 1% QTS may be a viable candidate for bone defect repair in view of anti-washout performance, setting time, antibacterial activity, and osteogenic activity shown in this study.

Iron-doped calcium silicate bone cement loaded with carboxymethyl chitosan for bone tissue engineering repair materials

Preparation and Characterization of Iron-Doped Tricalcium Silicate-Based Bone Cement as a Bone Repair Material

Enhanced Antibacterial Activity of Calcium Silicate-Based Hybrid Cements for Bone Repair.

Effects of tricalcium silicate/sodium alginate/calcium sulfate hemihydrate composite cements on osteogenic performances in vitro and in vivo

3D robocasting magnesium-doped wollastonite/TCP bioceramic scaffolds with improved bone regeneration capacity in critical sized calvarial defects

Study of the Mechanical Property of Magnetite/ Hydroxyapatite/ Chitosan Nano-Composite

A novel strategy for calcium magnesium phosphate/carboxymethyl chitosan composite bone cements with enhanced physicochemical properties, excellent cytocompatibility and osteogenic differentiation

A Bioactive Degradable Composite Bone Cement Based on Calcium Sulfate and Magnesium Polyphosphate

Methacrylated Carboxymethyl Chitosan Scaffold Containing Icariin-Loaded Short Fibers for Antibacterial, Hemostasis, and Bone Regeneration

3D-printed composite, calcium silicate ceramic doped with CaSO4·2H2O: Degradation performance and biocompatibility

Injectable Self-Setting Ternary Calcium-Based Bone Cement Promotes Bone Repair

Composition control in biphasic silicate microspheres on stimulating new bone regeneration and repair of osteoporotic femoral bone defect

The personalized design and customization of bone cement can be realized by adjusting the carbonization process of modified tricalcium silicate

Improvement of in vitro physicochemical properties and osteogenic activity of calcium sulfate cement for bone repair by dicalcium silicate

Calcium silicate cements prepared by hydrothermal synthesis for bone repair

In Vitro Physiochemical Properties of A Biomimetic Gelatin/Chitosan Oligosaccharide/Calcium Silicate Cement

A ternary calcium silicate bone cement with high mechanical properties and good operability

Novel highly bioactive and biodegradable gypsum/calcium silicate composite bone cements: from physicochemical characteristics to in vivo aspects

Tunicate cellulose nanocrystals reinforced modified calcium sulfate bone cement with enhanced mechanical properties for bone repair

Carboxymethyl chitosan-alginate enhances bone repair effects of magnesium phosphate bone cement by activating the FAK-Wnt pathway

Mesoporous calcium silicate and titanium composite scaffolds via 3D-printing for improved properties in bone repair