Preparation and Characterization of Iron-Doped Tricalcium Silicate-Based Bone Cement as a Bone Repair Material

Yanan Zhang,Jiapan Luan,Yin Zhang,Shuai Sha,Sha Li,Shanqi Xu,Dongqing Xu

DOI: https://doi.org/10.3390/ma13173670

IF: 3.4

2020-08-19

Materials

Abstract:Iron is one of the trace elements required by human body, and its deficiency can lead to abnormal bone metabolism. In this study, the effect of iron ions on the properties of tricalcium silicate bone cement (Fe/C3Ss) was investigated. It effectively solved the problems of high pH value and low biological activity of calcium silicate bone cement. The mechanical properties, in vitro mineralization ability and biocompatibility of the materials were systematically characterized. The results indicate that tricalcium silicate bone cement containing 5 mol% iron displayed good self-setting ability, mechanical properties and biodegradation performance in vitro. Compared with pure calcium silicate bone cement (C3Ss), Fe/C3Ss showed lower pH value (8.80) and higher porosity (45%), which was suitable for subsequent cell growth. Immersion test in vitro also confirmed its good ability to induce hydroxyapatite formation. Furthermore, cell culture experiments performed with Fe/C3Ss ion extracts clearly stated that the material had excellent cell proliferation abilities compared to C3Ss and low toxicity. The findings reveal that iron-doped tricalcium silicate bone cement is a promising bioactive material in bone repair applications.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The main problems that this paper attempts to solve are the deficiencies of traditional calcium silicate bone cement materials in terms of bioactivity, mechanical properties and degradation properties. Specifically:

1. **High pH problem**: Traditional calcium silicate bone cement will produce highly alkaline calcium hydroxide (Ca(OH)₂) during the hydration process, which will lead to an increase in the local pH value and may trigger an inflammatory response.

2. **Low bioactivity**: The bioactivity of traditional calcium silicate bone cement is low, which is not conducive to the repair and regeneration of bone tissue.

3. **Mechanical properties and degradation properties**: The mechanical strength of traditional calcium silicate bone cement is limited, and properties such as degradation rate and porosity need to be further optimized to better promote cell growth and bone tissue regeneration.

To solve these problems, researchers introduced iron ions (Fe³⁺) to be doped into tricalcium silicate (C₃S) to prepare a new type of iron - containing tricalcium silicate bone cement (Fe/C₃S). Through systematic in - vitro experiments, the effects of different iron contents on the setting time, compressive strength, porosity, anti - washing performance, pH value change, degradation performance and bioactivity of the bone cement material were studied. The research results show that the tricalcium silicate bone cement containing 5 mol% iron exhibits good self - setting, mechanical properties and in - vitro degradation properties, and has a lower pH value (8.80) and a higher porosity (45%), which is conducive to subsequent cell growth. In addition, the in - vitro immersion experiment also confirmed its good ability to induce the formation of hydroxyapatite (HAp), and the cell culture experiment shows that this material has excellent cell proliferation ability and low toxicity.

Therefore, this research shows that iron - containing tricalcium silicate bone cement is a potential bioactive material for bone repair.