3D robocasting magnesium-doped wollastonite/TCP bioceramic scaffolds with improved bone regeneration capacity in critical sized calvarial defects

Huifeng Shao,An Liu,Xiurong Ke,Miao Sun,Yong He,Xianyan Yang,Jianzhong Fu,Lei Zhang,Guojing Yang,Yanming Liu,Sanzhong Xu,Zhongru Gou

DOI: https://doi.org/10.1039/c7tb00217c

IF: 7.571

2017-01-01

Journal of Materials Chemistry B

Abstract:Using artificial biomaterials in bone regenerative medicine for highly efficient osteoconduction into the bone defect to decrease the bone healing time is still a challenge. In this research, magnesium (Mg)-doped wollastonite (similar to 10% Mg was substituted for calcium (Ca) in beta-CaSiO3) (CSi-Mg10) bioceramic scaffolds with ultrahigh mechanical strength were fabricated using ceramic ink writing three dimensional (3D) printing. To evaluate the potential of other additives on the new bone regeneration efficiency, beta-tricalcium phosphate (beta-TCP) was introduced to the CSi-Mg10 ceramic ink at a concentration of 15% and the biphasic bioceramic scaffolds (CSi-Mg10/TCP15) were also fabricated using 3D printing. The mechanical characterization indicated that introduction of beta-TCP led to nearly 50% mechanical decay, although the effect of the two heating schedules (one- and two-step sintering) on the compressive and flexural strengths of the scaffolds was significantly different. The bone regeneration results in critical sized calvarial defect of rabbits showed that the CSi-Mg10/TCP15 scaffolds displayed a markedly higher osteogenic capability than those on the CSi-Mg10 and beta-TCP scaffolds after eight weeks, and reached similar to 35% new bone tissue regeneration at 12 weeks postoperatively. These findings demonstrate that the CSi-Mg10/TCP15 bioceramic scaffolds can be well suited for stimulating in situ bone regeneration and for use in tissue engineering applications.