Abstract:Objective: One of the disadvantages of using CSC (calcium sulfate cement) in vivo is its weak osteogenic activity. Thus composite materials based on CSC have been recently studied. Silica-based mesoporous material (SBA-15) shows great potential for biological applications because of its functionalized surfaces and biocompatibility. We assumed that blending SBA-15 into CSC could improve the osteogenic activity of the CSC. Methods: SBA-15 was blended into CSC powder at a mass ratio of 5%, 10% and 20% to make a CSC/SBA composite. Four groups including CSC (pure CSC), CSC-5S (5% mass ratio), CSC-10S (10% mass ratio) and CSC-20S (20% mass ratio) group were designed. The cell adherence was assessed using the cell counting. The cell proliferation was determined by 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) assay. The osteogenic differentiation was evaluated using alkaline phosphatase (ALP) staining, alizarin red staining analysis, and the expression levels of osteogenic related genes, mainly ALP, collagen I (COL1), osteopontin and osteocalcin. An in vivo animal study was performed using the radius bone defect in a rabbit model. The micro computed tomography (CT) and histological evaluation were used to investigate bone formation. Results: The number of adhered cells on the CSC-10S and CSC-20S surface was higher than that on CSC and CSC-5S surface. The relative cell proliferation rate in CSC/SBA group was higher than that in CSC group. Compared with CSC and CSC-5S group, ALP staining in CSC-10S and CSC-20S group was increased. Alizarin red staining in the different CSC/SBA groups was higher than that in the CSC group. Higher expression levels of osteogenic differentiation-related genes were seen in cells grown on CSC/SBA composite. Micro CT and histological evaluation confirmed that CSC/SBA composite improved the efficiency of new bone formation in the bone defect. The above osteogenic activities were enhanced with increased mass ratio of SBS-15 in CSC/SBA composite. Conclusion: Incorporation of SBA-15 into CSC could greatly improve the osteogenic activity of CSC, implying the CSC/SBA composite are more beneficial to the bone repairing than pristine CSC.

Effects of tricalcium silicate/sodium alginate/calcium sulfate hemihydrate composite cements on osteogenic performances in vitro and in vivo

Design of novel organic-inorganic composite bone cements with high compressive strength, in vitro bioactivity and cytocompatibility.

Calcium Sulfate Cement Combined With Silica-Based Mesoporous Material For Bone Regeneration: In Vitro And In Vivo Study

3D robocasting magnesium-doped wollastonite/TCP bioceramic scaffolds with improved bone regeneration capacity in critical sized calvarial defects

A novel degradable tricalcium silicate/calcium polyphosphate/polyvinyl alcohol organic-inorganic composite cement for bone filling

Physicochemical properties and in vitro biocompatibility of a hydraulic calcium silicate/tricalcium aluminate cement for endodontic use.

Developing a biodegradable tricalcium silicate/glucono-delta-lactone/calcium sulfate dihydrate composite cement with high preliminary mechanical property for bone filling

Preparation of in situ forming and injectable alginate/mesoporous Sr-containing calcium silicate composite cement for bone repair

Iron-doped calcium silicate bone cement loaded with carboxymethyl chitosan for bone tissue engineering repair materials

Cytocompatibility and Cytotoxicity of a Novel Composite Bone Cement Material Composed of Chitosan Microsphere, Alpha-Tricalcium Phosphate and Silk Fibroin

Novel highly bioactive and biodegradable gypsum/calcium silicate composite bone cements: from physicochemical characteristics to in vivo aspects

Osteogenic Differentiation of Osteoblasts Induced by Calcium Silicate and Calcium Silicate/β‐tricalcium Phosphate Composite Bioceramics

Three-Dimensional Printing Of Beta-Tricalcium Phosphate/Calcium Silicate Composite Scaffolds For Bone Tissue Engineering

Investigation on structurally reinforced synthetic bone grafts via tricalcium silicate

A Composite of Cubic Calcium-Magnesium Sulfate and Bioglass for Bone Repair

A Bioactive Degradable Composite Bone Cement Based on Calcium Sulfate and Magnesium Polyphosphate

The Enhancement of Bone Regeneration by a Combination of Osteoconductivity and Osteostimulation Using Β-Casio3/β-ca3(po4)2 Composite Bioceramics.

In Vitro Degradability, Bioactivity And Primary Cell Responses To Bone Cements Containing Mesoporous Magnesium-Calcium Silicate And Calcium Sulfate For Bone Regeneration

A Novel Bi-Phase Sr-doped Magnesium Phosphate/calcium Silicate Composite Scaffold and Its Osteogenesis Promoting Effect

Effects of silicate-based composite material on the proliferation and mineralization behaviors of human dental pulp cells: An in vitro assessment

Composite bone graft of CaO-MgO-SiO2 glass-ceramics and CaSO4 ceramics for boosting bone formation rate