Physicochemical properties and in vitro biocompatibility of a hydraulic calcium silicate/tricalcium aluminate cement for endodontic use.

Weining Liu,Weiwei Peng,Yaqin Zhu,Jiang Chang

DOI: https://doi.org/10.1002/jbm.b.32690

2012-01-01

Abstract:This study sought to prepare a calcium silicate cement (CSC) with varying additions of tricalcium aluminate (Ca3Al2O6, C3A), and to find an optimal amount of C3A by evaluating the effect of C3A on the physicochemical and in vitro biological properties of the CS/C3A cement. The results indicated that the addition of C3A into CSC reduced the setting time and improved the compressive strength especially at the early stage of setting. However, the 15% C3A was too much for the CS/C3A system and did harm to its strength development. Furthermore, the CS/C3A cement was bioactive and biocompatible in vitro, and had a stimulatory effect on the cell growth, when the content of C3A was 5 or 10%. When compared with the commercially available Dycal (R), the CS/C3A cement was notably more compatible with the human dental pulp cells. Therefore, the CS/C3A cement with 5-10% C3A produced the best compromise between setting and in vitro biological properties, and may be a promising candidate for endodontic use. (c) 2012 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 2012.