Abstract:The effect of Bi2O3 on ZnO-based varistor ceramic sintered around 800 °C is still not fully understood, because most of the ceramic cannot reach full densification at this low-temperature. Therefore, (balanced) ZnO–0.5 mol% V2O5–0.5 mol% MnCO3–0.5 mol% Co2O3–0.5 mol% TiO2–xmol% Bi2O3 (x = 0, 0.01, 0.05, 0.1 and 0.2) ceramic was designed and prepared by the solid-state sintering at 800 °C. The effect of Bi2O3 variation on the microstructure and electrical nonlinearity of the sample material was studied by using methods of XRD SEM, STEM, EDS and E–J test. Bi2O3 can further activate the reaction at the interface between the V-rich liquid phase and ZnO grains during sintering. This enhanced interface reaction is the key reason to the extremely low-temperature sintering of the ceramic at 800 °C. The variation of Bi2O3 in the 0–0.2 mol% range barely influences the constituents of the ceramic, which consists of ZnO main phase and two other secondary phases: Zn3(VO4)2 and Zn2TiO4. Most of Bi2O3 tends to segregate at grain boundaries. As a result, a soaking time longer than 4 h is needed to allow Bi ions diffusing into enough grain boundaries and improving the nonlinearity of ZnO based varistor ceramic. The sample containing 0.01 mol% Bi2O3 and sintered at 800 °C for 8 h has the best properties of a 43.3 nonlinear coefficient, a 2300 V/mm breakdown voltage and a 0.13 mA/cm2 leakage current density.

Sintering mechanism and properties of ZnVMnNbO varistor ceramic and their evolutions by Ce–La doping

Microstructure and Electrical Properties of ZnO-Pr6O11-Dy2O3-Based Varistor Ceramics Doped with La2O3

Effect of Nb on Microstructure and Electric Properties of Nb and Ce doped TiO_2 Based Varistor Ceramics

Microstructure and Electrical Properties of ZnO-Pr<sub>6</sub>O<sub>11</sub>-Dy<sub>2</sub>O<sub>3</sub>-Based Varistor Ceramics Doped with La<sub>2</sub>O<sub>3</sub>

Effect of La<sub>2</sub>O<sub>3</sub> and CeO<sub>2</sub> on Nb<sub>2</sub>O<sub>5</sub> Doped TiO<sub>2</sub> Ceramic Varistors

Densification and Surge Current Performance of SnO_2-Sb_2O_3 Based Varistor Ceramics

Microstructure and Electrical Properties of Y(NO3)3·6H2O-doped ZnO–Bi2O3-based Varistor Ceramics

Sintering Temperature Dependence of Grain Boundary Resistivity in a Rare‐Earth‐Doped ZnO Varistor

Effect of SnO2 Doping on Microstructural and Electrical Properties of ZnO–Pr6O11 Based Varistor Ceramics

Optimization of Sintering Temperature and Doping Level of Cr2O3 in ZnO-Pr6O11-Based Varistor Ceramics

Influence of SnO2 on ZnO–Bi2O3–Co2O3 Based Varistor Ceramics

Effect of Bi2O3 on the ZnVMnCoTiO based varistor ceramic sintered at 800 °C

B<sub>2</sub>O<sub>3</sub>-Doped ZnO-Pr<sub>6</sub>O<sub>11</sub> Based Varistor Ceramics

The Effect of CeO2 Doping on the Electrical Properties of Nb-TiO2 Based Varistor Ceramics

Effect of Dy-doping or Nd-doping on the structure and properties of (Sr, Ba, Ca) TiO3-based varistor ceramics

Research method and mechanism analysis of a novel high-performance quaternary Zn–Sr–Co–Sb varistor ceramic

Structural and electrical properties of ZnO–V2O5–TiO2–Co2O3–MnO varistor ceramics with low sintering temperature

Microstructure and Electrical Properties of ZrO2-doped ZnO Varistor Ceramics

Structure modification and electrical properties by Mn2O3 dopant addition to SnO2 varistor system

Influence of Yb2o3 Doping on Microstructural and Electrical Properties of Zno-Bi2o3-Based Varistor Ceramics