Increasing the Porosity of Silica Particles by Reducing the Thickness of Nanochannel Walls and Producing an Additional System of Micropores

D. A. Eurov,D. A. Kirilenko,M. V. Tomkovich,M. A. Yagovkina,D. A. Kurdyukov

DOI: https://doi.org/10.1134/S002016852212007X

2023-03-01

Inorganic Materials

Abstract:We have developed a technique for the preparation of submicron spherical micro- and mesoporous silica particles via basic hydrolysis of organosilanes in an ethanol–water–ammonia mixture in the presence of cylindrical alkyl amine micelles. The particles synthesized in the presence of diethoxy(3-glycidyloxypropyl)methylsilane have been shown to contain cylindrical SiO 2 nanochannels with an inner diameter of 3 nm, characteristic of nanostructured M41S-type materials, but with a smaller wall thickness (0.5 instead of 0.7 nm). Owing to this, the specific surface area and volume of pores increased from 750 to 1200 m 2 /g and from 0.5 to 0.7 cm 3 /g, respectively. The addition of 3-(methacryloyloxy)propyltrimethoxysilane to the reaction mixture leads to further increase in these parameters (up to 1400 m 2 /g and 0.8 cm 3 /g) owing to micropore formation in the nanochannel walls.

materials science, multidisciplinary