Abstract:Surface finish or integrity is always an important problem threatening the safety service of components. In this study, the stress corrosion cracking (SCC) initiation behavior of Monel 400 alloy with different surface working treatments (mechanical grinding (TD specimen and PD specimen) and electrolytic polishing (EP specimen)) in hydrofluoric acid (HF) vapor were compared by conducting slow strain rate test (SSRT) and constant loading test (CLT). Although SSRT can evaluate the enhancement effect of mechanical grinding on SCC susceptibility, it cannot quantify its contribution to the crack initiation stage. The CLT shows the cracking initiation rate of different specimens in order of: EP specimen<TD specimen<PD specimen. For mechanical grinding specimens, local corrosion and cracks are inclined to nucleate at the groove shoulder zone rather groove bottom, which is mainly ascribed to the accumulation of higher corrosion degradation and higher defects at the groove shoulder. As the shoulder edge on the PD specimen is less constrained, it is easier to induce cracking under the synergistic action of stress concentration and preferential corrosion dissolution. While, the shoulder edge of the TD specimen is not a stress concentration position under tensile loading, and the micro-cracks formed by grinding are parallel to the loading direction, which is not conducive to the development of micro-cracks. Therefore, the crack initiation sensitivity of the TD specimen is lower than that of the PD specimen.

Revealing the effect of heat treatment on stress corrosion cracking behavior of Monel 400 alloy in hydrofluoric acid vapor environment

Detrimental Effect of Surface Mechanical Grinding on Stress Corrosion Behavior of Monel 400 alloy in Hydrofluoric Acid Vapor

Effect of Heat Treatment on the Stress Corrosion Cracking Behavior of Cast Mg-3Nd-3Gd-0.2Zn-0.5Zr Alloy in a 3.5 Wt% NaCl Salt Spray Environment

Stress Corrosion Cracking Behavior and Mechanism of Aging Treated Monel K500 Alloy in Flowing Seawater

Insights into the Superior Stress Corrosion Cracking Resistance of FeCrAl Alloy in High Temperature Hydrogenated Water: the Critical Role of Grain Boundary Oxidation

On the Stress Corrosion Crack Initiation Behaviour of Alloy 800 in High-Temperature Hydrogenated Water

The synergistic effect between fluoridation degradation and dislocation sliding on stress corrosion failure of Monel 400 alloy in HF vapor

Effect of Heat Treatment on Stress Corrosion Cracking, Fracture Toughness and Strength of 7085 Aluminum Alloy

Effect of Heat Treatment on Microstructure and Resistance to Stress Corrosion Cracking of Aluminum Alloy 2056

The SCC Initiation Behavior of Alloy 600 During the Transition of Hydrogenated/oxygenated Water Condition at Evaluated Temperature

Effect of Solution Treatment on the Fatigue Behavior of an As-Forged Mg-Zn-Y-Zr Alloy

Effect of heat treatment on stress corrosion cracking susceptibility of aluminum alloy 2519

Effects of Precipitation on the Stress Corrosion Crack Initiation of Alloy 718 in Simulated Pressurized Water Reactor Primary Environment

A Primary Study of the Effect of Hydrostatic Pressure on Stress Corrosion Cracking of Ti-6Al-4V Alloy in 3.5% NaCl Solution

Influence of heat treatment on the attack and stress corrosion cracking (SCC) resistance of Inconel alloy 690

Influence of Phase Dissolution and Hydrogen Absorption on the Stress Corrosion Cracking Behavior of Mg-7%Gd-5%Y-1%Nd-0.5%Zr Alloy in 3.5 Wt.% NaCl Solution

Effect of the Triangular Prism Dent on Stress Corrosion Cracking Behavior of Alloy 690TT Heat Transfer Tube in a Lead-Containing Alkaline Solution

Effects of heat treatment on corrosion fatigue and stress corrosion crack growth of additive-manufactured Alloy 800H in high-temperature water

Study of the Effect of Heat Treatment on Corrosion Property of the AlxCoCrFeNi High-Entropy Alloys (x = 0.3, 0.7, and 1) Prepared by Spark Plasma Sintering

Effects of Heat Treatment on High Temperature Mechanical Property and Corrosion Resistance of Hastelloy X Manufactured by Selective Laser Melting

Effects of Surface State and Applied Stress on Stress Corrosion Cracking of Alloy 690TT in Lead-containing Caustic Solution