Abstract:The practical application of MnFeOx catalyst is limited due to its narrow temperature window and poor resistance to alkali metal poisoning, such as K and Na. Alkali metal poisoning has always been a major factor in the deactivation of fixed-source denitration (deNOx) catalysts. Despite high activity at around 200(degrees)C , the catalyst's susceptibility to alkali metal poisoning hinders its effectiveness. In this study, a novel MnFeOx/H-Beta composite catalyst was prepared by the simple wet impregnation method. Beta zeolite, known for its large specific surface area compared to MnFeOx, special twelve-membered ring channel, and abundant acid sites, was introduced to adjust the acid and redox active sites. This resulted in MnFeOx/H-Beta having a wider temperature window and excellent resistance to K poisoning. Notably, the NOx conversion rate exceeded 80% between 180 and 460 C . K poisoning significantly reduces the acidity of the catalyst, as confirmed by various characterizations such as NH3TPD and NH3 adsorption in situ DRIFTs. After K poisoning, the total acid content of MnFeOx/H-Beta decreased from 14.99 to 9.47 mmol g(-1). The low acid content of MnFeOx allows the active sites to be easily covered by K, resulting in a reduction of the SCR performance, which can be attributed to the reduction of active nitrate species. The abundant acid sites of MnFeOx/H-Beta act as sacrificial sites and can coordinate with alkali metal K, thereby alleviating the poisoning of the catalyst to some extent. DFT calculations confirmed K binding to Bronsted acid sites on H-Beta zeolite, mitigating the detrimental impact of K on catalyst activity and lifetime. This research offers a pathway for designing efficient and alkali metal-resistant deNO(x )catalysts for real-world industrial applications.

Design Strategy of the MnO x Catalyst for SCR of NO with NH 3 : Mechanism of Lead Poisoning and Improvement Method

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

SO 2 and H 2 O Poisoning Resistance of Manganese Oxide-Based Catalysts for Low-Temperature Selective Catalytic Reduction of NO X

Discovering the Remarkable Denox Activity and Anti-K Poisoning of MnFeOx/H-Beta Composite Catalyst

Mechanistic Investigation of the Enhanced SO2 Resistance of Co-modified MnOx Catalyst for the Selective Catalytic Reduction of NOx by NH3

Promoting Effect of Polyoxometallic Acid Modification on the NH3-SCR Performance of Mn-Based Catalysts

Promoting effect of polyoxometallic acid modification on the NH 3 -SCR performance of Mn-based catalysts

Unveiling remarkable resistance to Pb poisoning over an Fe–Mo catalyst for low-temperature NH3-SCR: poison transforms into a promoter

Mechanism and regeneration of sulfur-poisoned Mn-promoted calcined NiAl hydrotalcite-like compounds for C3H6-SCR of NO

Low-temperature SCR of NOx by NH3 over MnOx/SAPO-34 prepared by two different methods: a comparative study

Design of robust Co-doped Mn3O4 spinel catalysts for selective catalytic reduction of NO with NH3 at low temperatures

Converting Poisonous Sulfate Species to an Active Promoter on TiO2 Predecorated MnOx Catalysts for the NH3-SCR Reaction

Enhancing Water Tolerance and N2 Selectivity in NH3-SCR Catalysts by Protecting Mn Oxide Nanoparticles in a Silicalite-1 Layer

Improved N2 Selectivity of MnOx Catalysts for NOx Reduction by Engineering Bridged Mn3+ Sites

Support promotion effect on the SO2 and K+ co-poisoning resistance of MnO2/TiO2 for NH3-SCR of NO

Unveiling the SO 2 Resistance Mechanism of a Nanostructured SiO 2 ( x )@Mn Catalyst for Low-Temperature NH 3 -SCR of NO

Highly Dispersed MnOx–FeOx Supported by Silicalite-1 for the Selective Catalytic Reduction of NOx with NH3 at Low Temperatures

Exploration of the Mn-O coordination regulated reaction stability of manganese oxides in NH 3 -SCR: Effect of deposited ammonium nitrates

A novel high activity MnXFe3−XO4 spinel catalyst for selective catalytic reduction of NO using NH3 prepared by a short process from natural minerals for low-temperature sintering flue gas: Effect of X value on catalytic mechanism

Manganese Oxide Catalysts Supported on Zinc Oxide Nanorod Arrays: A New Composite for Selective Catalytic Reduction of NOx with NH3 at Low Temperature

Mesoporous MnOx-CeO2 composites for NH3-SCR: the effect of preparation methods and a third dopant