Unveiling remarkable resistance to Pb poisoning over an Fe–Mo catalyst for low-temperature NH3-SCR: poison transforms into a promoter

Jincheng Mu,Jie Liu,Jiangzhou Qin,Xinyong Li,Baojun Liu

DOI: https://doi.org/10.1039/d2cy00630h

2022-01-01

Abstract:A heavy metal-resistant NO x catalytic reduction Fe–Mo catalyst was developed and a novel intrinsic activity enhancement mechanism by Pb species was originally demonstrated. Although lead (Pb) poisoning is a significant issue in the low-temperature selective catalytic reduction of NO x with NH 3 (NH 3 -SCR), the development of an effective Pb-resistant catalyst presents a challenge. Herein, a Fe–Mo catalyst composed of highly dispersed α-Fe 2 O 3 and β-FeMoO 4 was designed that exhibits remarkable resistance to Pb poisoning, achieving more than 90% NO x conversion at 225–400 °C (GHSV = 50 000 h −1 ) even with a Pb content of 20 wt%. More importantly, the poisoned catalysts show higher intrinsic activity and lower apparent activation energy compared to fresh sample. The characterization results indicate that the Pb species is captured by abundant Brønsted acid sites (Mo–OH) to form a PbMoO 4 phase, while barely influencing the Lewis acid sites and redox properties of the catalyst. The consumption kinetics of the adsorbed NH 3 based on in situ diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) confirmed that the surface PbMoO 4 species effectively boost the activation of the reactants, thus improving the inherent NH 3 -SCR reactivity through both Langmuir–Hinshelwood and Eley–Rideal pathways, which is the origin of the strong resistance against the high loading of Pb over the Mo–Fe catalyst. This work reveals a novel promotion mechanism of Pb species and provides a way in which to design a Pb-resistant low-temperature NH 3 -SCR catalyst.

chemistry, physical