Abstract:The evolution of phase composition and mechanical properties and the formation of oxide layers on Fe40–xNiCoCrAlx (x = 5 and 10 at.%) alloys in long-term oxidation at 900 and 1000°C were studied. In the initial cast state, depending on the aluminum content and valence electron concentration, the alloys contain only an fcc solid solution (VEC = 8 e/a) or a mixture of fcc and bcc phases (VEC = = 7.75 e/a). Thin continuous oxide scales containing Cr2O3 and NiCr2O4 spinel formed on the surface of both alloys oxidized at 900°C for 50 h. A further increase in the annealing time to 100 h leads to the formation of aluminum oxide Al2O3 in the scale on the Fe30Ni25Co15Cr20Al10 alloy, having high protective properties. An increase in the oxidation temperature to 1000°C results in partial failure of the protective layer on the alloy with 10 at.% Al. Long-term holding at 900°C (100 h) + 1000°C (50 h) does not change the phase composition of the Fe35Ni25Co15Cr20Al5 alloy matrix, being indicative of its high thermal stability. In the two-phase Fe30Ni25Co15Cr20Al10 alloy, the quantitative ratio of solid solutions sharply changes: the amount of the bcc phase increases from 4 to 54 wt.% and its B2-type ordering is observed. The mechanical characteristics of the starting alloys and those after long-term high-temperature annealing were determined by automated indentation. The hardness (HIT) and elastic modulus (E) of the cast Fe35Ni25Co15Cr20Al5 alloy are equal to 2 and 147 GPa, respectively, and decrease to 1.8 and 106 GPa after a series of long-term annealing operations. The Fe30Ni25Co15Cr20Al10 alloy shows the opposite dependence: HIT increases from 2.5 in the initial state to 3.1 GPa after annealing and E decreases from 152 to 134 GPa. This indicates that the Fe30Ni25Co15Cr20Al10 alloy is promising as a high-temperature oxidation-resistant and creep-resistant material.

Fatigue Resistance of the Sheets of Heat-Resistant Titanium Alloys

Thermal Oxidation Behaviour of Ti6Al7Nb and Ti6Al4V Alloys

A Study of the Back Stress and the Friction Stress Behaviors of Ti-6Al-4V Alloy During Low Cycle Fatigue at Room Temperature

Surface Characterization of Thermally Oxidized Titanium Alloys

Fatigue and Corrosion Fatigue of Thermally Oxidized Ti6Al4V Alloy

Fatigue Behavior of Titanium Alloy Ti-4Al-2V under High Cycle Loading at Elevated Temperature

High-temperature fatigue behavior of TC17 titanium alloy and influence of surface oxidation

High-temperature Fatigue Property of Ti46Al8Nb Alloy with the Fully Lamellar Microstructure

Characteristics of heat resistant alloys Ti10Nb45Al and Ti18Nb48Al

Isothermal and thermomechanical fatigue behavior of Ti-2Al-2.5Zr titanium alloy

Effect of Microarc Oxidation Coating on Fatigue Performance of Ti–Al–Zr Alloy

Influence of Thermal Oxidation Temperature on the Microstructural and Tribological Behavior of Ti6Al4V Alloy

Influence of Thermal Oxidation Duration on the Microstructure and Fretting Wear Behavior of Ti6Al4V Alloy

Structural State of High-Entropy Fe40–xNiCoCrAlx Alloys in High-Temperature Oxidation

Effect of Oxygen Variation on High Cycle Fatigue Behavior of Ti-6Al-4V Titanium Alloy

Effect of Low-Temperature Oxidation and Oxynitriding on the Fretting Corrosion of VT22 Titanium Alloy

Impact of thermal oxidation parameters on micro-hardness and hot corrosion of Ti-6Al-3Mo-2Nb-2Sn-2Zr-1.5Cr alloy

Microstructural effects on the high-cycle fatigue and fracture behaviors of Ti-6Al-4V alloy

High Temperature Isothermal and Thermomechanical Fatigue on A Molybdenum-Based Alloy

The Effect of heat treatment on the fatigue properties of titanium-tantalum alloy

Damage Analysis of High Temperature Isothermal and Thermomechanical Fatigue on A Tzm Alloy