The Influence of (bi0.5na0.5)0.7sr0.3tio3 Doping on the Structure and Electrical Properties of [0.93Nanbo3-0.07Bi(mg0.5sn0.5)o3] Ceramics
Guo Yun-Feng,Wang Jun-Xian,Wang Ze-Xing,Li Jia-Mao,Chen Li-Ming
DOI: https://doi.org/10.7498/aps.74.20240833
IF: 0.906
2025-01-01
Acta Physica Sinica
Abstract:As a key component in capacitors, sodium niobate-based dielectric energy storage materials have the advantages of low relative density, lead-free, low cost and excellent energy storage density, and can meet the significant demand for electronic components to develop towards miniaturization, harmlessness, integration and light weight. Therefore, they have received extensive attention and constantly research from the scientific community in recent years. In this paper, by introducing both Bi(Mg0.5Sn0.5)O3 and (Bi0.5Na0.5)0.7Sr0.3TiO3 components into NaNbO3 ceramics, the conventional solid-phase sintering method was used to prepare (1-x)[0.93NaNbO3-0.07Bi(Mg0.5Sn0.5)O3]-x(Bi0.5Na0.5)0.7Sr0.3TiO3 (Abbreviated as (1-x)(NN-BMS)-xBNST, 0.00 ≤ x ≤ 0.3)relaxation ferroelectric ceramics, and characterized the ceramics using X-ray diffraction, scanning electron microscopy, UV spectroscopy and Raman spectroscopy to study the effect of (Bi0.5Na0.5)0.7Sr0.3TiO3 doping on the physical phase composition, microstructure, as well as electrical properties of NaNbO3 ceramics, such as dielectric and energy storage. (1-x)(NN-BMS)-xBNST ceramics exhibit a single perovskite structure, with an increase in cell volume followed by a decrease, and coexistence of Pbma and Pnma phases. (1-x)(NN-BMS)-xBNST ceramics exhibit a dense microstructure and clear grain boundaries at the optimal sintering temperature. The average grain size first increased to 4.73 μm, then decreased to 2.17 μm, and then increased to 3.06 μm. A smaller grain size and a larger bandgap width are beneficial for improving the breakdown strength. 0.75(NN-BMS)-0.25BNST ceramic demonstrated excellent dielectric temperature stability (25 ~ 160 ℃，Δε/ε25℃ ≤ ±15%) and dielectric frequency stability, which can meet the EIAZ8U standard and hence work in a special environment (high temperature/high frequency). Meanwhile, 0.75(NN-BMS)-0.25BNST ceramic achieved good energy storage performances at high field strength (390 kV/cm): recoverable energy density(Wrec) = 2.73 J/cm3, energy storage efficiency (η) = 82.6%, and high temperature stability in the temperature range of 20~100 ℃. Research has shown that 0.75(NN-BMS)-0.25BNST ceramics have broad application prospects in lead-free dielectric energy storage capacitors.