Temperature dependences and rate effects on Mode II fracture toughness determined by punch-through shear technique for granite

Tubing Yin,Xiaosong Tan,You Wu,Zheng Yang,Mingjian Li
DOI: https://doi.org/10.1016/j.tafmec.2021.103029
IF: 4.374
2021-08-01
Theoretical and Applied Fracture Mechanics
Abstract:<p>Most studies of thermal effects on rock fracture have focused on Mode I, while the temperature-dependence and loading rate effect on Mode II fracture are rarely involved. We present the static and dynamic punch-through shear (PTS) tests, implemented on the INSTRON 1342 and the modified split Hopkinson pressure bar (SHPB) system respectively, as the approaches for determining the Mode II fracture toughness (<em>K</em><sub>II</sub><em><sub>C</sub></em>) of PTS specimens at a series of thermal treatments and loading rates. As any macroscopic characteristic of rock is related to its microscopic or mesoscopic structures and properties, the SEM technique is thus applied to observe the mesoscopic morphology of heated and tested specimens. The fracture mode in the static and dynamic PTS tests is verified to be the dominant Mode II by fracture surface SEM observations. The results show that static <em>K</em><sub>II</sub><em><sub>C</sub></em> (<span class="math"><math>KIICS</math></span>) increases with the thermal treatment temperature while static Mode I fracture toughness (<em>K</em><sub>I</sub><em><sub>C</sub></em>) is almost unchanged within 200°C, and they all decrease substantially from 200°C to 600°C. Moreover, the dynamic <em>K</em><sub>II</sub><em><sub>C</sub></em> (<span class="math"><math>KIICD</math></span>) at each thermal treatment temperature appears obvious loading rate effect. The strengthening effect of high loading rate on <span class="math"><math>KIICD</math></span> is almost unchanged below 400°C, while the thermal effect on <span class="math"><math>KIICD/KIICS</math></span> becomes apparent when the temperature reaches 600°C. The SEM observation displays that almost no cracks initiating within 200°C, and the growth of obvious intergranular and transgranular cracks commence at about 400°C and 600°C, respectively. Besides, reticular cracks start to generate at 400°C. As such, the mesoscopic characteristics at different thermal treatment temperatures are in accord with the variations of physical and mechanical parameters.</p>
engineering, mechanical,mechanics
What problem does this paper attempt to address?