Effect of pulse current parameters on electroplastically assisted dry cutting performance of W93NiFe alloy

DOI: https://doi.org/10.1007/s00170-022-10762-7

2023-01-04

Abstract:Tungsten alloys have excellent properties such as high strength, high hardness, high melting point, and high specific gravity, which have been widely used in many cutting-edge scientific fields such as aerospace and military. In order to solve the problems of poor surface quality and severe tool wear in tungsten alloy cutting, conventional dry turning and electroplastically assisted dry turning with different electrical parameters were carried out to study the effects of electroplasticity on surface roughness, surface defects, tool wear, and chip morphology of W93NiFe alloy. The results showed that the electroplastically assisted dry turning process improved the surface quality of W93NiFe alloy. The surface roughness value decreases gradually with the increase of pulse voltage and reaches the minimum value at the pulse voltage of 80 V, with the maximum reduction of 38.94% compared with conventional dry turning. However, too high pulse voltage causes an increase in the surface roughness value. When the pulse voltage was increased from 80 to 90 V, the surface roughness increased by 29.63%. At a pulse voltage of 70 V, the surface roughness value did not change much for different pulse current frequency conditions. Compared to conventional dry turning, electroplastically assisted cutting reduced the degree of machined surface defects in the material and tool wear, but it could lead to the formation of built-up edge at the tool tip. After the pulsed current was applied, the chip curl radius and pitch were smaller, and it was easier to form strip chips with longer transverse lengths. The results provide a reliable reference for electroplastically assisted cutting in the future.

engineering, manufacturing,automation & control systems