Abstract:In this study, friction stir welding (FSW) was employed to join AA3003-H18 sheets by incorporating in situ Al-Cu intermetallic compounds within the stir zone. The FSW process was carried out under three distinct conditions: (I) without applying powder, (II) by introducing Cu powder, and (III) by incorporating Cu-Al mixed powder (50 vol.% Cu, 50 vol.% Al). The powder was embedded into the gap between two sheets. Subsequently, two-pass FSW, involving both forward and backward movements, was conducted with a rotational speed of 1200 rpm and traverse speed of 100 mm/min across all three experimental conditions. In the second and third conditions, the formation of in situ intermetallic compounds occurred through a solid-state reaction between Cu particles and Al within the stir zone. Examination of the stir zone through optical and electron microscopic studies revealed that the utilization of Cu-Al mixed powder resulted in finer and more uniformly distributed Cu clusters and Al-Cu intermetallics than samples welded with Cu powder alone. Notably, the stir zone of samples incorporating Cu-Al mixed powder exhibited finely dispersed, completely gray Al-Cu intermetallic particles, whereas those with only Cu powder displayed predominantly coarse core-shell particles in the microstructure. The introduction of Cu-Al mixed powder during FSW resulted in a stir zone with an average hardness of 74 HB, showing a 14% increase compared to the cases where Cu powder alone was added (65 HB). Tensile tests, conducted in both transverse and longitudinal directions on the FSWed samples, did not exhibit a consistent trend across the three mentioned conditions. Transverse tensile strength consistently ranged between 107 and 110 MPa, with joint efficiency varying from 52% to 54%. However, the longitudinal tensile strength of the joint with added Cu-Al mixed powder (158 MPa) surpassed those welded with Cu powder alone (134 MPa).

Regularities of Structure Formation During Friction Stir Processing of CuAl9Mn2 Copper Alloy with Addition of Tungsten Powder to the Surface Layer

Surface CuAl9Mn2/W Composites Prepared by Multipass Friction Stir Processing: Microstructures, Phases, and Mechanical and Tribological Properties

Microstructural Evolution and Mechanical Properties of Dissimilar Al–Cu Joints Produced by Friction Stir Welding

Effect of Microstructure Refinement on Surface Morphology and Dynamic Mechanical Properties of W-Cu Alloys

Effect of Tool Speed on Microstructure Evolution and Mechanical Properties of Friction Stir Welded Joints of Al-Mg-Si Alloy with High Cu Content

Microstructure Evolution and Mechanical Properties of Friction Stir Spot Welded Dissimilar Aluminum-Copper Joint

Microstructural Characterisation and Mechanical Properties of Friction Stir Welded Joints of Aluminium Alloy to Copper

Effect of Tool-Workpiece Relative Position on Microstructure and Mechanical Properties of Al-Cu Dissimilar Friction Stir Weld

Microstructure Evolution and Mechanical Properties of Friction Stir Welded Al–Cu–Li Alloy

Microstructure evolution and frictional wear behavior of Al‐18Si‐4Mg‐2Mn‐0.5Fe‐xCu alloys fabricated by laser additive manufacturing

Microstructural characterization and mechanical properties of micro friction stir welded dissimilar Al/Cu ultra-thin sheets

Effect of Dispersing In Situ Al-Cu Intermetallic Compounds on Joint Strength in Friction Stir Welding of AA3003-H18 Sheets

Statistical and Metallurgical Analysis of Dissimilar Friction Stir Spot Welded Aluminum/Copper Metals

Regularities of Structure Formation and Properties of Composite Materials Based on Aluminum–Manganese Bronze Produced by Electron Beam Additive Manufacturing with the Addition of Iron, Nickel, and Tungsten Powders During Printing

Microstructural Characterisation and Mechanical Properties of Dissimilar AA5083-copper Joints Produced by Friction Stir Welding

Microstructures and Mechanical Properties of Friction-Stir Welding Joint of Al-Cu-Li Alloy

Correlation Between Microstructures and Mechanical Properties of High-Speed Friction Stir Welded Aluminum Hollow Extrusions Subjected to Axial Forces

Microstructures and Properties of Friction Stir Welded Al-Cu Lap Joints

Structure-property Characteristics of Al-Cu Joint Formed by High-Rotation-speed Friction Stir Lap Welding Without Tool Penetration into Lower Cu Sheet

Study on Microstructure and Properties of 1060 Aluminum Alloy/T2 Cu Friction Stir Welding Joints

Influence of Fe and Al2O3 Addition on the Mechanical and Tribological Properties of Cu-Based Composites