Abstract:All-solid-state lithium batteries (ASSBs) are considered like the next generation of electrochemical energy storage devices because of their safety and their high energy density up to 400Wh/kg. The all-solid-state battery is composed of a positive electrode (e.g., NMC (Li(Ni 1∕3 Mn 1∕3 Co 1∕3 )O 2 )), a negative one (Li), and a solid electrolyte, which is the critical component, composed of inorganic compound and/or solid polymer electrolyte (SPE) [1]. On the one hand, SPE have the advantage of an easy shaping with the technique already used in the manufacture of batteries and their flexibility allows obtaining a good interface with the electrode materials [2]. On the other hand, inorganic compounds generally have high ionic conductivity (10 -3 S/cm), they are stable electrochemically vs Li/Li + and their transport number is close to 1 to promote the diffusion/migration of Li + ions only. In order to combine the advantages of both types of materials, hybrid materials have been designed [3]. First, a new adaptable polymer matrix based on PEO derivatives has been developed. A solvent-free synthesis has been designed from liquid and commercial precursors Poly(ethylene glycol) methyl methacrylate (PEGM) and Poly(ethylene glycol) dimethacrylate (PEGDM). These latter were copolymerized with Lithium 3-[(trifluoromethane)sulfonamidosulfonyl] propyl methacrylate (MTFSLi). The anion TFSI - is thus grafted to the PEO network, allowing exclusively the diffusion of the Li + ion. This polymer matrix can be thus classified as single-ion conductor. In addition, the proportions between PEGM and PEGDM, acting as crosslinker, can be easily tuned. The PEGDM proportion controls the cross-linking density which modifies not only the glass transition temperature (Tg), but also the storage modulus (E’) and the free volume, and consequently the ionic conductivity of the polymer matrix which is the main property required for SPE. Finally, a ratio of PEGM:PEGDM (80:20) allows obtaining homogeneous SPE, self-standing and soft at room temperature, amorphous with a Tg of -41°C. The EO/Li ratio was then modulated in single-ion networks with the MTFSLi proportion, and an optimum in ionic conductivity of 2.10 -7 S/cm @25°C has been measured for EO/Li ratio of about 20. The transport number measured by the Bruce and Vincent method [4] was t + =1,0 for the single ion conductor, demonstrating the effective grafting of the counter anion. This value has been validated by measuring the diffusion coefficients of 7 Li and 19 F in NMR. To our knowledge, this is the first time a real unity transport number is reported in the literature for a polymer electrolyte. Moreover, the electrochemical stability of this single ion system extends from 0 to 6V vs Li + /Li. These experiments suggest the interest of using the single-ion polymer in the formulation of composite positive electrode with high potential cathode materials, due to its stability in potential. Li metal is considered the ultimate anode for Li-batteries. The long-term electrochemical stability has been evaluated in symmetric Li/polymer electrolyte/Li cell. The cell is cycled at a constant current density of 0.2 mA/cm 2 . After 200 h of cycling the voltage reaches solely 2V. Accordingly, the grafting of the anion to the network limits an overpotential in the cell, allowing a more stable system over time. Second, the garnet Li 6.4 La 3 Zr 2 Al 0.2 O 12 (LLZO) of the oxide family was associated to the previous polymer matrix. This garnet presents a high conductivity (10 -4 S/cm @ 25°C), a good chemical stability not only against lithium metal but also against air and humidity, which is not the case of sulphides homologues. A 3D-fibrous network obtained by the electrospinning method was carried out with a solution containing the inorganic precursors, a polymer and an appropriate solvent [5]. Then this membrane is calcined at 850°C to obtain the 3D fibrous network of LLZO. The resulting self-standing porous inorganic material (~80% of porosity) exhibits a conductivity of the order of 10 -6 S/cm @25°C. It was then impregnated with the polymer matrix precursors by capillarity and following by a polymerization. A self-standing membrane as thin as 80 μm containing 9%vol of LLZO was obtained. The conductivity of this hybrid membrane is comparable to that of the polymer (10 -7 S/cm @ 25°C). The resulting hybrid is mainly polymeric where the ionic conduction was realized by the polymeric matrix and the inorganic acts as a mechanical reinforcement. Preliminary results on high content of LLZO hybrid will also be presented, where a synergy of the both components is observed. [1] Janek . Nature Energy. 2016. Vol 1(9)p.16141. [2] Yue. Energy Storage Materials. 2016. Vol 5p.139-164. [3] Zheng. Chem Soc Rev. 2020. Vol 49p.8790-8839. [4] Bruce. Solid State Ion . 1988. Vol 28–30 p.918–922. [5] A. La Monaca . Electrochemistry Communications. 2019. Vol 104p.106483. Figure 1

Performance of solid-state Li-ion conducting battery using biopolymer electrolyte based on agar–agar/lithium chloride

Performance study of sodium alginate (SA) with lithium chloride (LiCl)-based solid-state membrane as an electrolyte in electrochemical device application

Development and characterization of biopolymer electrolyte based on gellan gum for the fabrication of solid-state sodium-ion battery

Characterization of biodegradable solid polymer electrolyte system based on agar-NH4Br and its comparison with NH4I

Development of sodium-ion conducting biopolymer electrolyte membrane based on Agar-Agar with sodium perchlorate (NaClO4) using ethylene carbonate (EC) as a plasticizer for primary Na-ion battery

A physicochemical elucidation of sodium perchlorate incorporated alginate biopolymer: toward all-solid-state sodium-ion battery

Potential of UV-Curable Poly(Glycidyl Methacrylate-co-Ethyl Methacrylate)- Based Solid Polymer Electrolyte For Lithium Ion Battery Application

Bio-host pectin complexed with dilithium borate based solid electrolytes for polymer batteries

Preparation and Characterization of Biopolymer Electrolyte Membranes Based on LiClO4-Complexed Methyl Cellulose as Lithium-ion Battery Separator

Preparation and Study of a Simple Three-Matrix Solid Electrolyte Membrane in Air

Investigations on Na-ion conducting electrolyte based on sodium alginate biopolymer for all-solid-state sodium-ion batteries

Study of PVAc-PMMA-LiCl polymer blend electrolyte and the effect of plasticizer ethylene carbonate and nanofiller titania on PVAc-PMMA-LiCl polymer blend electrolyte

(Digital Presentation) Post-Treatment Study on Blended Polymer for Solid-State Lithium Batteries

A Flexible Solid Polymer Electrolyte based Polymerized Ionic Liquid for High Performance Solid‐State Batteries

Influence of binary lithium salts on 49% poly(methyl methacrylate) grafted natural rubber based solid polymer electrolytes

Conception of Hybrid Organic-Inorganic Membrane as New Electrolyte in All Solid-State Battery

Solid-State Lithium Batteries with In Situ Polymerized Acrylate-Based Electrolytes Capable of Electrochemically Stable Operation at 100 °C

Nanophase separated, grafted alternate copolymer styrene-maleic anhydride as an efficient room temperature solid state lithium ion conductor

Fabrication of solid polymer electrolyte based on carboxymethyl cellulose complexed with lithium acetate salt as Lithium‐ion battery separator

Study on PVDF-HFP/PMMA/CMC Blended Polymer as Membrane for Lithium-Ion Batteries

Ultrathin polymer electrolyte film prepared by in situ polymerization for lithium metal batteries