Abstract:A large amount of air is drawn into the high-temperature plasma jet during the atmospheric plasma spraying (APS) process because it operates in an atmospheric environment, thus oxidizing metal-spray particles. The oxide inclusion resulting from in-flight droplet oxidation inhibits the metallurgical bonding between lamellae in the coating, which limits the applications of plasma-sprayed metal coatings. In this study, a novel approach to create oxide-free molten droplets is proposed by adding B to the CuNi powder to achieve sacrificial oxidation of B in the high-temperature droplet and protect the alloy elements from oxidation. Two powders of CuNi2B and CuNi4B were prepared to deposit the coatings via APS. The effect of B content and spray distance on the microstructure, as well as the O content of CuNi coating, was studied using methods such as SEM, EDS, XRD, and inductively coupled plasma-optical emission spectrum (ICP-CES). The results show that the droplet can be heated to more than 1900 degrees C, and the introduction of B in the powder can inhibit the oxidation of alloy elements in the high-temperature droplet during flight, thus reducing the oxygen in the CuNi coating. Moreover, the deoxidizing effect is affected by the B content of the droplet. Using 4%B CuNi alloy powder and increasing spray distance, the oxide in the coating is reduced. The oxygen in the coating is introduced via oxidation after droplet deposition, and the oxygen content of the coating prepared using the optimized spraying process is reduced to 0.43%, which is considerably lower than 3.5% of CuNiIn coating. An increase in the spray distance and a reduction in B content of CuNi powder, which contains 1.83%B, to 0.5% is insufficient to inhibit the oxidation of the alloying elements of the in-flight particles. The result yields a critical B content of approximately 0.5% for high-temperature droplet oxidation protection. The increase in the B content decreases the melting point, as well as the oxidation of the alloy, thus enhancing the metallurgical bonding between CuNi particles and improving the compactness of the coating. In addition, with the increase in the B content of the coating through the powder composition design and process parameters control from 0.26% to 3.61%, the microhardness of CuNi coating increases from 151 HV0.2 to 457 HV0.2.

Oxidation behavior and mechanism of Ag-9.8Sn-1.3Bi-0.4Cu alloy powders in different oxidant

Influence of oxidant and sample state on oxides distribution of Ag-4.93Sn-3.56In alloy powders

Oxidation kinetics characteristics of Ag-5.08Sn-3.14Sb alloy powders in different oxidizing atmosphere

Thermal Oxidation Behaviour of Ti6Al7Nb and Ti6Al4V Alloys

Influences of Tin Oxide Surface Modification on the Morphology and Performance of Sintered Ag/SnO2 Composite Powders

Phase Structure Analysis of AgCd and AgSn Alloy Powders

Influences of Metal Oxide Additions on the Morphology of Sintered AgSnO2 Composite Powders

The Behavior and Effect of CuO in Ag/SnO2 Materials

XPS study of the oxidation behavior of the Cu3Sn intermetallic compound at low temperatures

Oxidation Behavior Of Sn-9zn-3bi-Xcr Solders Under High-Temperature Exposure

Oxidation Behavior and Intermetallic Compounds Growth of Sn-Ag-Bi-Cr Lead-free Solder

Dynamic Investigation of Cu50at%Au (001) Alloy Film Nano-oxidation by in Situ UHV TEM

On Effect of Microstructure about Bi for Agsno2 Compositions by Reaction Synthesis

Spreading Dynamics and Interfacial Characteristics of Sn-3.0Ag-0.5Cu-xBi Melting on Cu Substrates

The Oxidation Resistance of Cu-Ag Alloy Nanopowders Prepared by Induction Plasma Technology

Oxidation Characteristics of Nickel-Based Superalloy Powders Exposed at Ambient Condition

Investigation of synchrotron X-ray induced oxidation of Ag–Cu thin-film

Study on the Mechanism of Melting Oxidation of Zn-9Al-2.5Mg-Be Alloy

Oxidation mechanism of MAX phases (Ti3AlC2 powders) with and without Sn doping

Oxide Cleaning Effect of In-Flight CuNi Droplet During Atmospheric Plasma Spraying by B Addition

Interface-level thermodynamic stability diagram for in situ internal oxidation of Ag(SnO2)p composites