Abstract:The caking and adhesion of intermediate product on reactor surfaces during TiO2 production via the NaOH molten salt method are a serious problem. The consolidation of intermediate product can lead to low heat transfer efficiency and low titanium fractional conversion. Furthermore, frequent cleaning is generally required. An anti-caking method that can be applied during low-grade titanium slag decomposition in the NaOH system was studied. The method, which involves the two-step reaction of low-grade titanium slag with molten NaOH without the introduction of additives, can significantly reduce the extent of caking. The NaOH and low-grade titanium slag mixture was first reacted at 350°C for 60min. The temperature was then increased to 550°C in 40min. Finally, the mixture was reacted at 550°C for 75min. The effects of the reaction temperatures, NaOH-to-slag mass ratio and the reaction time on the titanium extraction were investigated. The Brunauer–Emmett–Teller (BET) surface area and apparent density were used to characterize the extent of caking. In the low grade titanium slag, silicate phase prior to pseudobrookite phase reacts with molten NaOH at 350°C in the process of two-step molten reaction and formed sodium silicate. Microstructural and Fourier transform infrared (FT-IR) absorption results show that the firstly formed sodium silicate did not diffuse into the entire reaction system and powder-shaped intermediate product was formed. Approximately 97% of titanium in the titanium slag could be extracted under the optimal reaction conditions. In addition, the content of TiO2 obtained in the product reached 99.3%.

Phase conversion and removal of impurities during oxygen-rich alkali conversion of high titanium slag

Anti-caking in the production of titanium dioxide using low-grade titanium slag via the NaOH molten salt method

Simultaneous removal of Cr(III) and V(V) and enhanced synthesis of high-grade rutile TiO2 based on sodium carbonate decomposition

Extraction of vanadium and enrichment of titanium from modified Ti-bearing blast furnace slag

Extraction of Valuable Metals from Titanium-bearing Blast Furnace Slag by Acid Leaching

Mechanism of Melt Separation in Preparation of Low-Oxygen High Titanium Ferroalloy Prepared by Multistage and Deep Reduction

Effect of Al2o3 Addition on the Precipitated Phase Transformation in Ti-Bearing Blast Furnace Slags

A novel preparation of titanium dioxide from titanium slag

Removal of magnesium and calcium from electric furnace titanium slag by H3PO4 oxidation roasting–leaching process

Recovery of titanium, aluminum, magnesium and separating silicon from titanium-bearing blast furnace slag by sulfuric acid curing—leaching

Recovery of titania from high titanium slag by roasting method using concentrated sulfuric acid

Novel Process for Titanium Dioxide Production from Titanium Slag: NaOH-KOH Binary Molten Salt Roasting and Water Leaching

Study of the oxygen reduction of low valent titanium in high titanium slag by microwave rapid heating

Combined Effect of SiO2 and O2 on the Crystallization Behavior of Modified Ti-Bearing Blast Furnace Slag

Effect of oxidization on enrichment behavior of TiO2 in titanium-bearing slag

Recovery of Titanium Compounds from Ti-enriched Product of Alkali Melting Ti-bearing Blast Furnace Slag by Dilute Sulfuric Acid Leaching

Synergistic Leaching of Titanium, Aluminum, and Magnesium Components during Dilute Acid Pressure Treatment of High-Titanium Blast Furnace Slag

The Conversion of Calcium-Containing Phases and Their Separation with NaCl in Molten Salt Chlorinated Slags at High Temperature

Changes of Two Phase Composition in Phase Separation Process of Na2o-Cao-Al2o3-B2o3-Sio2-Tio2 System

Alkali fusion using sodium carbonate for extraction of vanadium and tungsten for the preparation of synthetic sodium titanate from spent SCR catalyst