Abstract:The alkali metal poisoned CuNbTi and VWTi catalysts were prepared by wetness impregnation method. Poisoning effects of various K2O mass ratios (0.1%-2%) on CuNbTi and VWTi catalysts were studied, respectively. CuNbTi exhibited an excellent alkali metal resistance that 2%K2O-CuNbTi still remained 80% NOx conversion efficiency and 98% N-2 selectivity while 2%K2O-VWTi was completely deactivated. Moreover, different alkali metals (K, Na, Ca, Mg) with the same molar ratio were doped on CuNbTi. The poisoned degree followed the order: K2O > Na2O > CaO > MgO. Then 2%K2O-CuNbTi and 2%K2O-VWTi were selected for follow-up study. To understand the poisoning mechanism, further investigations were performed by SEM, XRD, N-2-physisorption, XPS, EPR, NH3-TPD, Py-IR, H-2-TPR, in situ DRIFTS characterizations and DFT calculations. The particle of CuNbTi and VWTi agglomerated and the surface area decreased after 2%K2O loading. Loss of acid sites and drop of reducibility resulted in the deactivation of 2%K2O-VWTi. By contrast, experimental and computational results indicated that the alkali resistance of 2%K2O-CuNbTi was mainly due to the interaction between Ti2NbOx support and K atoms that K atoms were preferentially bound to Nb OH and Nb=O with a lower bonding energy of -2.33 eV- -2.83 eV when Cu atoms were coordinated to Ti=O with a binding energy of -1.54 eV. This protected the active copper species from linking to K2O and the weak acid sites were preserved with the increasing isolated Cu2+. Ti2NbOx weakened the impact of potassium on NH3 adsorbing over the catalyst while the preserved copper species provided adsorption sites and redox ability for NH3-SCR reaction. Hence, the synergetic effect of copper and niobium species contributed to the alkali metal resistance. Ti2NbOx trapped the potassium and retained active copper species over 2%K2O-CuNbTi catalyst while potassium deactivated both TiO2 and active vanadium species on 2%K2O-VWTi catalyst. Meanwhile, both Eley-Rideal (E-R) and Langmuir-Hinshelwood (H-L) mechanisms with adsorbed NH3 coordinated to the Lewis acid sites and bidentate nitrate as the dominating intermediate species existed during the NH3-SCR reaction procedure over 2%K2O-CuNbTi at 225 degrees C.

Revealing the Promotion Effects of Nb on Alkali Resistance of FeVO4/TiO2 Catalysts for NOx Reduction

New Insights into the Relationships Between Performance and Physicochemical Properties of FeOx–NbOx Mixed Oxide Catalysts for the NH3-SCR Reactions

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

Novel FeVO4 catalyst modified with NbTiOx for efficient selective catalytic reduction of NOx with NH3

Insight into the Alkali Resistance Mechanism of FeMoTiO x Catalysts for NH 3 Selective Catalytic Reduction of NO: Self-Defense Effects of MoO x for Alkali Capture

New Insight into Alkali Resistance and Low Temperature Activation on Vanadia-Titania Catalysts for Selective Catalytic Reduction of NO

Promotional effect of aluminum doping on the sulfated Fe2O3 catalyst in selective catalytic reduction of NO with NH3

The Alkali Resistance of CuNbTi Catalyst for Selective Reduction of NO by NH3: A Comparative Investigation with VWTi Catalyst

The Co-Effect of Sb and Nb on the SCR Performance of the V2O5/TiO2 Catalyst

Modulating the Activity and SO2 Resistance of Α-Fe2o3 Catalysts for NH3-SCR of NOx Via Crystal Facet Engineering

Promotional effect of phosphorus modification on improving the Na resistance of V2O5-MoO3/TiO2 catalyst for selective catalytic reduction of NO by NH3

Acidified SiO2 Supported Fe-based Bimetal Oxide Catalyst with Resistance to High-Level Alkali Poisoning for CO Selective Catalytic Reduction of NO Removal of NOx

Improvement of Al2O3 on the Multi-Pollutant Control Performance of NOx and Chlorobenzene in Vanadia-Based Catalysts

Adsorption-Induced Active Vanadium Species Facilitate Excellent Performance in Low-Temperature Catalytic NO x Abatement

New insight on optimization of acid promoter over Fe/Zr catalyst for selective catalytic reduction of NO with NH3

Modulating the Activity and SO 2 Resistance of α-Fe 2 O 3 Catalysts for NH 3 -SCR of NO x via Crystal Facet Engineering

Substitution of WO3in V2O5/WO3–TiO2by Fe2O3for Selective Catalytic Reduction of NO with NH3

Bimetallic Modification of Mnfeo X Nanobelts with Nb and Nd for Enhanced Low-Temperature De-No X Performance and So2 Tolerance

The Reaction of Poisonous Alkali Oxides with Vanadia SCR Catalyst and the Afterward Influence: A DFT and Experimental Study

Effect of Nb‐doping on the MnFeOx catalyst for NH3‐SCR reaction at low‐temperature

Enhancement of Low-Temperature Activity of Γ-Fe2o3-Modified V2o5-Moo3/Tio2 Catalysts for Selective Catalytic Reduction of Nox with Nh3