Efficient degradation and Ni recovery from Ni-EDTA wastewater by Ni/GAC electrodes
Tong Yang,Haoran Lu,Yiming Qin,Yulong Liu,Xu Han,Wenyan Liang
DOI: https://doi.org/10.1016/j.jwpe.2024.106410
IF: 7
2024-11-02
Journal of Water Process Engineering
Abstract:Ni-EDTA, a heavy metal complex commonly encountered in electroplating wastewater, is challenging to degrade due to its inherent structural stability. Hence, in this study, we employed a three-dimensional granular electrodes system (3DES) to effectively treat Ni-EDTA and simultaneously recover Ni. Ni/GAC electrode was prepared with granular activated carbon (GAC) as carrier and Ni as catalyst through electrodeposition. X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR) and X-ray photoelectron spectroscopy (XPS) analysis confirmed that nickel present on Ni/GAC consisted of Ni 0 , NiO and Ni(OH) ads . Results from linear sweep voltammetry (LSV), cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) demonstrated an exceptional hydrogen evolution overpotential, reaching 340 mV at 10 mA cm −2 , with the electrochemical surface area (ECSA) as high as 266.2 cm 2 and charge transfer resistance (R ct ) as low as 10.78 Ω. The optimal decomplexation percentages of Ni-EDTA, TCNi, and the recovery of TNi, were determined to be 95 %, 92 %, an d 88 %, respectively, under the conditions of 5.00 mA cm −2 , 3 mM potassium persulfate (KPS), initial pH of 2.76, Ni:EDTA ratio of 1:1. CV indicated that Ni-EDTA can be directly reduced through acquiring two electrons or oxidized on Ni/GAC. In addition, electron spin resonance (ESR) and quenching experiments indicated that the crucial roles played by OH, SO 4 − and H*. Based on the chemical probe experiments, the relative contributions of direct electron transfer, OH, SO 4 − and H* were calculated to be 7.6, 34.0, 18.0 and 40.4 %, respectively. In conclusion, the Ni/GAC + KPS system shows a promising strategy to treat Ni-EDTA wastewater.
engineering, chemical, environmental,water resources