Multi-energy Field-Assisted Water Jet Strengthening 2519a Dynamic Impact Behavior and High Cycle Fatigue Enhancement Mechanism
Ping Zhang,Yeran Gao,Xiujie Yue,Yajie Sun,Hanping Zhou,Jinlong Zhang
DOI: https://doi.org/10.1007/s11837-024-06944-1
2024-11-06
JOM
Abstract:The purpose of this study is to investigate the dynamic mechanical properties of the 2519a aluminum alloy and the effects of water jet (WJ) strengthening on its fatigue performance. Initially, the stress–strain behavior of 2519a aluminum alloy under different strain rates and temperatures was studied using the Split Hopkinson Pressure Bar (SHPB) test, and the Johnson–Cook (J–C) constitutive model for the 2519a aluminum alloy was established. The numerical analysis model for WJ strengthening and the fatigue life after WJ strengthening was constructed using finite element software ABAQUS and Fe-safe, and the numerical results were verified through experiments. The findings indicate that the dynamic mechanical properties of the 2519a specimens exhibit strain rate sensitivity and temperature softening behavior. The surface roughness of the specimens after WJ strengthening is positively correlated with the jet velocity, with the average surface roughness being approximately 1.1 μm, 1.6 μm, and 1.9 μm, respectively. The maximum residual compressive stress in the specimens is positively correlated with the jet velocity; as the jet velocity increases from 150 mm/s to 210 mm/s, the induced maximum residual compressive stress is approximately 102.5 MPa, 161.8 MPa, and 174.5 MPa, respectively. The depth of the maximum residual compressive stress is 102.9 μm, 102.9 μm, and 114.2 μm, respectively. With the increase in jet velocity, the increase in the amplitude of the maximum residual compressive stress gradually decreases, but the depth of the maximum residual compressive stress significantly increases. Therefore, it is considered that controlling the jet velocity and optimizing the jet parameters can achieve a better induction of residual compressive stress. Additionally, the fatigue life cycle count of the specimens is positively correlated with the WJ velocity, with the cycle count increasing by 118% and 116% at the same WJ velocity interval, and the fatigue cycle count of the specimens after WJ-210 mm/s strengthening is 137% higher than that after WJ-150 mm/s strengthening. The crack fracture morphology after WJ strengthening was also analyzed. This study pioneers the use of WJ for surface treatment of 2519a aluminum alloy, providing a viable reference scheme for effectively and economically improving the fatigue performance of 2519a aluminum alloy.
materials science, multidisciplinary,metallurgy & metallurgical engineering,mining & mineral processing,mineralogy