Abstract:To prevent primary water stress corrosion cracking (PWSCC), water jet peening (WJP) has been used on the welds of Ni-based alloys in pressurized water reactors (PWRs). Before WJP, the welds are machined and buffed in order to conduct a penetrant test (PT) to verify the weld qualities to access, and microstructure evolution takes place in the target area due to the severe plastic deformation. The compressive residual stresses induced by WJP might be unstable under elevated temperatures because of the high dislocation density in the compressive stress layer. Therefore, the stability of the compressive residual stresses caused by WJP was investigated during long-term operation by considering the microstructure evolution due to the working processes. The following conclusions were made: The compressive residual stresses were slightly relaxed in the surface layers of the thermally aged specimens. There were no differences in the magnitude of the relaxation based on temperature or time. The compressive residual stresses induced by WJP were confirmed to remain stable under elevated temperatures. The stress relaxation at the surface followed the Johnson-Mehl equation, which states that stress relaxation can occur due to the recovery of severe plastic strain, since the estimated activation energy agrees very well with the self-diffusion energy for Ni. By utilizing the additivity rule, it was indicated that stress relaxation due to recovery is completed during the startup process. It was proposed that the long-term stability of WJP under elevated temperatures must be assessed based on compressive stresses with respect to the yield stress. Thermal elastic-plastic creep analysis was performed to predict the effect of creep strain. After 100 yr of simulated continuous operation at 80% capacity, there was little change in the WJP compressive stresses under an actual operating temperature of 623 K. Therefore, the long-term stability of WJP during actual operation was analytically predicted.

Improving the corrosion and stress corrosion cracking resistance of 316 L stainless steel in high temperature water by water jet cavitation peening

Progress on microstructure and residual stress evolution and corrosion behavior in SP-, LSP- and WJP-treated austenitic stainless steels

Comparison of the effect of water jet cavitation peening on stress corrosion cracking behavior of nickel-based alloy 600 and alloy 182 in high temperature water

Study on the process of abrasive water jet peening for 316L stainless steel

Effects of Chloride and Oxygen on Stress Corrosion Cracking of Cold Worked 316/316L Austenitic Stainless Steel in High Temperature Water

Prevention of Stress Corrosion Cracking in Welded Joint of Type 304 Stainless Steel by Laser Peening

A Research on the Corrosion and Stress Corrosion Cracking Susceptibility of 316L Stainless Steel Exposed to Supercritical Water

Effect of inhomogeneous microstructure on the stress corrosion cracking behavior of 316LN stainless steel weld joint under high-temperature and high-pressure water small punch test

Effect of Ultrasonic Shot Peening on Microstructure and Corrosion Properties of GTA-Welded 304L Stainless Steel

Utilizing the water hammer effect to enhance the mechanical properties of AISI 304 welded joints

Influence of laser peening processing on SCC sensitivity in weld joint of 304 type stainless steel

Effect of Laser Shock Peening on Stress Corrosion Cracking of TC4/2A14 Dissimilar Metal Friction Stir Welding Joints

Investigation Of The Influence Of Shot Peening On Stress Corrosion Cracking Of Stainless Steel Welded Joints

Effect of Ultrasonic Impact Treatment on the Stress Corrosion Cracking of 304 Stainless Steel Welded Joints

Effect of Ultrasonic Shot Peening on Stress Corrosion of 304 Austenitic Stainless Steel

Long-Term Stability of Residual Stress Improvement by Water Jet Peening Considering Working Processes

Environmentally Assisted Cracking of Forged 316LN Stainless Steel and Its Weld in High Temperature Water

Combined effects of machining-induced residual stress and external load on SCC initiation and early propagation of 316 stainless steel in high temperature high pressure water

Study on the fatigue performance and Residual Stress of subsurface fluid flow of 2519a aluminum alloy based on water jet peening

Effect of shot peening on surface characteristics and high-temperature corrosion behaviour of super 13Cr martensitic stainless steel

Stress Corrosion of Austenitic Stainless Steel 316L in High Temperature Water