Abstract:The release and transformation mechanism of residual stress contributes to the improvement of metal materials' processing and performance, enhancing their structural stability, surface integrity, and fracture resistance. This paper focuses on the Ultrasonic Impact Treatment-Solid Particle Entrainment by Waterjet (UIT-SPEWJ) composite surface modification of 7075-T6 aluminum alloy, investigating the effects of UIT-SPEWJ process parameters (jet pressure and target distance) on the alloy's surface quality, roughness, microhardness, residual stress, and the evolution mechanism of microstructure. The results indicate that the 7075-T6 aluminum alloy modified by UIT-SPEWJ mainly exhibits a "meteorite crater" effect, accompanied by significant smearing and ploughing phenomena. Surface roughness shows a trend of first decreasing and then increasing with the rise of jet pressure and target distance. The minimum surface roughness, 0.852 μm, is achieved at a jet pressure of 25 MPa and a target distance of 7.5 mm. The microhardness of the samples modified by UIT-SPEWJ gradually decreases from the surface to the substrate with increasing depth. The hardened layer depths of the samples UIT-SPEWJ-1–6 after modification are approximately 174 μm, 226 μm, 200 μm, 196 μm, 176 μm, and 172 μm, respectively. After UIT, SPEWJ, and UIT-SPEWJ surface modifications, the surface of 7075-T6 aluminum alloy mainly exhibits compressive residual stress (CRS). The surface residual stress σ_srs of samples modified by UIT and SPEWJ are approximately 195.161 and 215.752 MPa, respectively. The surface residual stresses of UIT-SPEWJ-1–6 samples are significantly improved to 277.089, 529.499, 393.615, 459.261, 368.084, and 220.635 MPa, respectively, with UIT-SPEWJ-2 sample having the highest surface residual stress, which is 2.7 and 2.4 times that of UIT and SPEWJ modified surfaces. Samples modified by UIT-SPEWJ present significant dislocation phenomena, and the precipitated phases mainly include the needle-like metastable phase η', as well as the equilibrium phase η (MgZn2) with a rod-like structure. At lower jet pressures and larger target distances, the 7075-T6 aluminum alloy exhibits a continuous PFZ with a size of approximately 12–23 nm. As jet pressure increases and target distance decreases, discontinuous grain boundary precipitate bands appear, sized around 8–17 nm. Moreover, when the jet pressure is 25 MPa and the target distance is 7.5 mm, the grain boundary precipitated phases are more dispersed.

Pre-mixed abrasive waterjet peening with post-low stress milling process and the effect of process parameters on the surface integrity of TC11 titanium alloy

Influence of submerged micro-abrasive waterjet peening on surface integrity and fatigue performance of TA19 titanium alloy

Surface strengthening in confined spaces: A novel deflecting abrasive waterjet peening for improving the surface integrity of nickel-based superalloys GH4169

Evaluation of Surface Integrity in 18CrNiMo7-6 Steel after Multiple Abrasive Waterjet Peening Process

Submerged deflecting abrasive waterjet peening for improving the surface integrity and solid particle erosion resistance of Ti-6Al-4V alloy

Evaluating surface mechanical properties and wear resistance of Ti-6Al-4V alloy subjected to ultrasonic pulsed waterjet peening

Titanium Alloy Milling Using Abrasive Water Jet for Repair Application: Modifications in Surface Quality and Material Integrity Following Plain Water Jet Cleaning

Research on the multilevel energy decrement strategy for abrasive waterjet peening Ti6Al4V

Effects of Ultrasonic Shot Peening on Fatigue Behavior of TA15 Titanium Alloy Fabricated by Laser Melting Deposition

The effects of submerged laser peening, cavitation peening, and shot peening on the improvement of the torsional fatigue strength of powder bed fused Ti6Al4V produced through laser sintering

Study on the fatigue performance and Residual Stress of subsurface fluid flow of 2519a aluminum alloy based on water jet peening

Modelling and experimental study of surface treatment in abrasive waterjet peening of Nickel-based superalloy: Inverse problem

Microstructure Evolution and Numerical Modeling of TC4 Titanium Alloy during Ultrasonic Shot Peening Process

Ultrasonic peening-waterjet composite surface modification of 7075-T6 aluminum alloy for residual stress release and transformation mechanism

Use of an Abrasive Water Cavitating Jet and Peening Process to Improve the Fatigue Strength of Titanium Alloy 6Al-4V Manufactured by the Electron Beam Powder Bed Melting (EBPB) Additive Manufacturing Method

Performance Analysis of 7075 Aluminum Alloy Strengthened by Cavitation Water Jet Peening at Different Scanning Speeds

Effects of Laser Shock Peening on Microstructure and Properties of Ti–6Al–4V Titanium Alloy Fabricated via Selective Laser Melting

Study on multi-field composite strengthening, surface integrity, and microstructural evolution mechanism of 7075-T6 aluminum alloy

Influence law and optimization analysis of technological parameters of TC4 titanium alloy on water cavitation peening

Surface residual stress, micro-hardness and geometry of TC6 titanium alloy thin-wall parts processed by multiple oblique laser shock peening

Effects of heat treatment combined with laser shock peening on wire and arc additive manufactured Ti17 titanium alloy: Microstructures, residual stress and mechanical properties