Abstract:Copper-nickel alloys have received much attention in the last decades due to their high electrical, thermal, mechanical, and magnetic properties which mainly depend on their composition. In this paper, copper-nickel alloy coatings onto indium tin oxide substrate were elaborated by electrodeposition in pulsed current mode with optimized current density and deposition time. The electrodeposition is subsequently followed by thermal treatment under controlled atmosphere. The surface morphology and the chemical analysis of the elaborated coatings were assessed by scanning electron microscopy associated to x-ray microanalysis. Their structural analysis was performed by x-ray diffraction, and the Vickers microhardness test was conducted to examine their mechanical properties. Moreover, the adhesive strength of the copper-nickel coatings was evaluated using a progressive scratch test, while a multi-pass scratch test was employed to assess their wear resistance. The results showed that the copper-nickel coating obtained with optimized current density (− 20 mA/cm 2 ) and heat treated at 600 °C for 1 h under controlled atmosphere exhibits high mechanical properties; the microhardness increases from 133 to 280 HV, and the adhesion strength from 32 to 203 MPa. On the other hand, optimized electrodeposition conditions followed by thermal treatment led to thinner characteristic XRD pics of Cu-Ni coating indicating an increase in crystallinity from 12 nm to 44 nm. Mechanical characteristics underlined a high resistance to scratches, a decrease in the friction coefficient, and an increase in the dissipated energy which reaches 20 J for heat-treated Cu-Ni coating. These results highlighted a homogeneity in morphology, and low porosity improving the CuNi coatings adhesion strength to the substrate.

The effect of pre-heat and post-heat treatment on the hardness and blackening process of electroless NiP deposits on titanium alloy

Surface Characterization of Thermally Oxidized Titanium Alloys

Effects of Heat Treatment on Structure Transformation of Cr/Al Composite Coatings

Effect of Heat-Treatment on the Thermal and Mechanical Stability of Ni/Al2O3 Nanocrystalline Coatings

Mechanical Properties of the TiAlSiN Coatings by Post Heat Treatments

Effect of vacuum heat treatment on NiCrAlY coating/titanium alloy substrate system

Tribological Behaviors of Electroless Nickel-Boron Coating on Titanium Alloy Surface

Preparation of Black High Absorbance and High Emissivity Thermal Control Coating on Ti Alloy by Plasma Electrolytic Oxidation

Oxidation issues during heat treatment and effect on the tribo-mechanical performance of electroless Ni-P–Cu deposits

The Effect of Heating Time and Heating Temperatures to Layer Thickness and the Glossiness Level of a Surface in Blackening Coating Process

Heat Treatment Effects on the Microstructural and Mechanical Properties of Electrodeposited Cu-Ni Coatings

Effect of different heat-treated temperatures upon structural and abrasive performance of Ni-TiN composite nanocoatings

Mechanical, Tribological, and Electrochemical Evaluation of NiCrAlMoFe Thermally Sprayed Coatings Subject to Post-treatments

Effect of Heat Treatment on Microstructure and Corrosion Resistance of Electrodeposited Nickel-Tungsten Alloy Coating

Effects of hydrothermal treatment on physicochemical and anticorrosion properties of titanium nitride coating on pure titanium

Effects of Al Addition and Annealing on Microstructure and Properties of Ni-Ti Coatings Synthesized on SUS 316L Stainless Steel Substrates Using Mechanical Alloying Method

Formation of Al2O3 coatings on NiTi alloy by micro-arc oxidation method

Effect of Heat Treatment with Sol-gel Method on Surface of Ni-Cr Alloy after Coating Ti

Microstructural response and wear behaviour of Ti-6Al-4V impregnated with Ni/Al2O3 + TiO2 nanostructured coating using an electric arc

The Microstructure and Tribological Behavior of Ultrasonic Electroless Ni-P Plating on TC4 Titanium Alloy with Heat-Treatment

Black PEO Coating with Enhanced Thermal Stability on Titanium Alloy and Its Thermal Control Properties