Abstract:Electrospun anatase-phase TiO2 nanofibers with desired morphological structure and relatively high specific surface area are expected to outperform other nanostructures (e.g., powder and film) of TiO2 for various applications (particularly dye-sensitized solar cell and photo-catalysis). In this study, systematic investigations were carried out to prepare and characterize electrospun anatase-phase TiO2 nanofibers with different morphological structures (e.g., solid, hollow/tubular, and porous) and specific surface areas. The TiO2 nanofibers were generally prepared via electrospinning of precursor nanofibers followed by pyrolysis at 500°C. For making hollow/tubular TiO2 nanofibers, the technique of co-axial electrospinning was utilized; while for making porous TiO2 nanofibers, the etching treatment in NaOH aqueous solution was adopted. The results indicated that the hollow/tubular TiO2 nanofibers (with diameters of ∼300–500nm and wall-thickness in the range from tens of nanometers to ∼200nm) had the BET specific surface area of ∼27.3m2/g, which was approximately twice as that of the solid TiO2 nanofibers (∼15.2m2/g) with diameters of ∼200–300nm and lengths of at least tens of microns. Porous TiO2 nanofibers made from the precursor of Al2O3/TiO2 composite nanofibers had the BET specific surface area of ∼106.5m2/g, whereas porous TiO2 nanofibers made from the precursor of ZnO/TiO2 composite nanofibers had the highest BET specific surface area of ∼148.6m2/g.

Preparation and characterization of anatase titanium dioxide fibre by electrospinning

Fabrication and Photocatalytic Activity of Tio2 Nanofiber Membrane

Preparation and Characterisation of Ultrafine and Uniform Tio2 Nanofibres

Synthesis and characterization of rutile-typed TiO2 porous hollow nanofibres via electrospinning

Electrospun anatase-phase TiO2 nanofibers with different morphological structures and specific surface areas.

Preparation and Photocatalysis of Mesoporous Tio2 Nanofibers Via an Electrospinning Technique

Fabrication and characterization of electrospun titania nanofibers

Study on the Preparation and Photocatalytic Properties of Au/TiO2 Composite Fibers

Electrospun TiO2–SiO2 Fibres with Hierarchical Pores from Phase Separation

Synthesis of Titania Fibers by Electrospinning and Its Photocatalytic Degradation Properties

Convenient Fabrication of Carbon-Doped Titania Nanofibres by Electrospinning

Electrospun Mesoporous Titanium Dioxide Fibers

Fabrication of porous titanium dioxide fibers and their photocatalytic activity for hydrogen evolution

General Strategy for Fabricating Thoroughly Mesoporous Nanofibers.

Fabrication of TiO 2 /sio 2 Hybrid Fibers with Tunable Internal Porous Structures

Preparation of Highly Porous Tio2 Nanotubes and Their Catalytic Applications

Electrospinning Synthesis of SiO2-TiO2 Hybrid Nanofibers with Large Surface Area and Excellent Photocatalytic Activity

Synthesis of TiO2 Nanofiber and Microsphere by Electrospinning and Their Performance of Photocatalytic Production Hydrogen

Facile Synthesis Via Electrospinning of a Tetraethoxysilane/Polyvinylpyrrolidone Sol and Characterization of Ultrafine Crystalline SiO2 Nanofibers

Preparation and Characterization and Photocatalytic Properties of TiO2 Fibre

Titanium Dioxide Fibers Prepared by Sol–gel Process and Centrifugal Spinning