Electrospinning synthesis of N-doped TiO2 fiber membranes and its enhanced photocatalysis performance

Jie Gao,Lingfan Zhang,Junchao Qian,Feng Chen,Wenqing Zhang

DOI: https://doi.org/10.1007/s11696-020-01286-z

IF: 2.146

2020-07-16

Chemical Papers

Abstract:N-doped TiO2 fiber membranes were prepared by electrospinning method and adsorptive chitosan was added as a nitrogen source. The obtained TiO2 fiber membranes were analyzed by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, Raman spectroscopy and X-ray photoelectron spectroscopy (XPS). The results show that the film has adsorption properties; furthermore, the morphology of the TiO2 fiber with a chitosan content of 0.5 g after calcination provides the best catalytic performance; An anatase–rutile titania was found in the oxidized fiber film found in the Raman spectrum TiO2; XPS demonstrated that the introduction of chitosan could replace N atom with partial lattice oxygen in TiO2. Moreover, the degradation rate of methylene blue of the material was about 60–80% after 4-h reaction, and the maximum degradation rate was achieved by nanofiber film with chitosan concentration of 0.5 g.