Effect of scanning speed on the high-temperature oxidation resistance and mechanical properties of Inconel 625 alloys fabricated by selective laser melting

Weiying Huang,Yutong Li,R.E.N. Yanjie,Jinshan Sun,Zhonghu Xia,Libo Zhou,Cong Li,Jian Chen,Yan Niu,Yuhang Zhao

DOI: https://doi.org/10.1016/j.vacuum.2022.111447

IF: 4

2022-10-02

Vacuum

Abstract:The effect of scanning speed (600–1200 mm/s) on the high-temperature oxidation resistance and high-temperature mechanical properties of selective laser melting processed Inconel 625 samples was studied at 1000 °C, 1atm of pure oxygen and vacuum environment, respectively. The high-temperature tensile test showed that the ultimate tensile strength (UTS) of sample IV(171.31 MPa) with a scanning speed of 1050 mm/s was lower than that of sample III(185.34 MPa) with 900 mm/s, which was related to the low proportion of (low angle grain boundaries)LAGBs and its highest density. Sample IV showed the best plasticity (14.5%) mainly due to the slip promoted by the high proportion of high angle grain boundaries (HAGBs). After oxidation for 40 h, the oxide scale of all samples consists of a Cr 2 O 3 oxide layer and nickel-rich spinel oxide. The samples with a density of less than 99% had the worst oxidation resistance due to manufacturing defects that accelerated the inward diffusion of oxygen. When the density was larger than 99%, the oxidation performance of alloys mainly affected by their distinctive microstructure. According to thermogravimetric analysis, the sample IV exhibited the lowest parabolic oxidation rate, which could attribute to its weak texture, grain refinement, and a high proportion of CSL boundaries.

materials science, multidisciplinary,physics, applied