Abstract:In this study, IN-718 samples were printed using laser powder bed fusion (LPBF) process to investigate the effect of printing parameters (in terms of Volume Energy Density, (VED)), printing orientation, heat treatment and test temperature on the microstructure and mechanical properties. Tensile properties were evaluated using small-scale tensile specimens extracted from samples printed with 15 different processing parameters (by varying scan speed and scan power) in two print orientations (XY and XZ plane), in three microstructural conditions (as-printed (AP), printed + solution treated and aged (STA), printed + hot isostatically pressed (HIP) + STA), at two different temperatures (room temperature and 650 °C). The mechanical properties obtained from testing of small-scale tensile specimens were compared with results obtained from testing of specimens following ASTM E8 standard, to understand effect of specimen size on mechanical properties. Based on microstructural analysis, it was observed that below a VED value of 50 J/mm 3 , the conduction region prevailed, with the presence of irregular lack of fusion porosities. In VED range of 50–100 J/mm 3 , transition prevailed with highly dense samples (over 99 % of theoretical density) with minimal porosity. Above a VED of 100 J/mm 3 , keyhole regime prevailed with the presence of spherical keyhole porosities. STA heat treatment improved YS and UTS to ∼1200 and ∼1400 MPa, respectively, while reducing ductility to ∼15 %. HIP + STA had similar effect on tensile properties as STA heat treatment. Based on tensile strength data, it was observed that HIP is not essential for parts printed with optimum parameters. Sample size in the present study was found to have an insignificant effect on tensile properties. In conclusion, the study provides an insight into the role played by printing parameters, printing orientation, and post-processing on defects, microstructures and thereby on the mechanical properties.

Effect of Laser Power and Scanning Speed on the Microstructure and Mechanical Properties of SLM Fabricated Inconel 718 Specimens

Effect of Laser Energy Density on the Microstructure, Mechanical Properties, and Deformation of Inconel 718 Samples Fabricated by Selective Laser Melting

Effects of laser scanning speed and building direction on the microstructure and mechanical properties of selective laser melted Inconel 718 superalloy

Effect of Laser Energy Density on the Microstructure and Microhardness of Inconel 718 Alloy Fabricated by Selective Laser Melting

Effect of Layer-Wise Varying Parameters on the Microstructure and Soundness of Selective Laser Melted INCONEL 718 Alloy

Effect of Scanning Strategies on the Microstructure and Mechanical Properties of Inconel 718 Alloy Fabricated by Laser Powder Bed Fusion

Mechanical properties and microstructure evolution of selective laser melting Inconel 718 along building direction and sectional dimension

High-throughput investigation of laser powder bed fabricated Inconel 718 alloy: Fabrication, microstructure and performance

Effect of Preheating Temperature on Microstructural and Mechanical Properties of Inconel 718 Fabricated by Selective Laser Melting

Effect of Welding Speed on Microstructure and Mechanical Properties of Selective Laser Melting Inconel 625 Alloy Laser Welded Joint

Microstructures and Mechanical Behaviors of Additive Manufactured Inconel 625 alloys via Selective Laser Melting and Laser Engineered Net Shaping

Formability, Microstructure and Properties of Inconel 718 Superalloy Fabricated by Selective Laser Melting Additive Manufacture Technology

Effect of parameters on quality of IN718 parts using laser additive manufacturing

Effect of heat treatment on the microstructure and mechanical properties of Inconel 718 processed by selective laser melting

Effect of heat treatment on microstructure and mechanical properties of selective laser melted Inconel 718 alloy

On the Microstructure and Tensile Properties of Inconel 718 Alloy Fabricated by Selective Laser Melting and Conventional Casting

Mechanical properties of laser powder bed fusion processed Inconel alloy IN718 in different heat treatment conditions through small scale specimen testing

Effects of laser scanning speed on the microstructure and mechanical properties of 2205 duplex stainless steel fabricated by selective laser melting

Influence of Selective Laser Melting Additive Manufacturing Parameters in Inconel 718 Superalloy

Microstructural evolution and mechanical properties of Inconel 718 alloy manufactured by selective laser melting after solution and double aging treatments

Mechanical Properties and Microstructure of Inconel 718 Lattice Structures Produced by Selective Laser Melting Process