Analysis on technology and defects of fracture splitting of automobile engine connecting rod

Hongyu Yang,Shuqing Kou,Wenqiang Gao,Peng Zhang

DOI: https://doi.org/10.1177/0954405414539493

2014-07-24

Abstract:The principle of connecting rod (con-rod) fracture splitting was analyzed, and the microscopic morphology of fracture surface was observed using scanning electron microscope. Crack initiation and propagation during the fracture splitting of con-rod process was numerically simulated. The effects of the bolt hole on the fracture splitting force and distribution of stress and strain were investigated. Typical location of fracture splitting defects and why they were generated were analyzed, and methods were proposed to avoid them. The results show that the nature of con-rod fracture splitting is a mode I quasi-brittle fracture, and the position of crack initiation can be found during the analysis process. Existence of the bolt hole is helpful to optimize fracture splitting technology and improve product quality, and the optimized range of bolt hole position was achieved based on simulation result. Moreover, defects such as steps, break-outs, usually occur between the bolt hole wall and outer edge of the con-rod big end in that two cracks converged and propagation velocity was slow in this region. The fracture splitting defects can be reduced or avoided when the outer shape of the fracture surface is a circular arc.