Abstract:Through low‐temperature oxidization of polycrystalline Cu foils, rapid preparation of large‐area single‐crystal Cu(111) (up to 320 cm2) is achieved within 60 min, thanks to the transformation of the thin CuxO layer to a Cu(111) seed layer. Large‐size high‐quality graphene films are synthesized on the single‐crystal Cu(111), and the graphene/Cu(111) composites exhibit enhanced thermal conductivity and ductility compared to their polycrystalline counterpart. The controlled preparation of single‐crystal Cu(111) is intensively investigated owing to the superior properties of Cu(111) and its advantages in synthesizing high‐quality 2D materials, especially graphene. However, the accessibility of large‐area single‐crystal Cu(111) is still hindered by time‐consuming, complicated, and high‐cost preparation methods. Here, the oxidization‐temperature‐triggered rapid preparation of large‐area single‐crystal Cu(111) in which an area up to 320 cm2 is prepared within 60 min, and where low‐temperature oxidization of polycrystalline Cu foil surface plays a vital role, is reported. A mechanism is proposed, by which the thin CuxO layer transforms to a Cu(111) seed layer on the surface of Cu to induce the formation of a large‐area Cu(111) foil, which is supported by both experimental data and molecular dynamics simulation results. In addition, a large‐size high‐quality graphene film is synthesized on the single‐crystal Cu(111) foil surface and the graphene/Cu(111) composites exhibit enhanced thermal conductivity and ductility compared to their polycrystalline counterpart. This work, therefore, not only provides a new avenue toward the monocrystallinity of Cu with specific planes but also contributes to improving the mass production of high‐quality 2D materials.

Seamless Stitching of Graphene Domains on Polished Copper (111) Foil

Oxide-assisted Growth of Scalable Single-Crystalline Graphene with Seamlessly Stitched Millimeter-Sized Domains on Commercial Copper Foils.

Large-Area Synthesis of High-Quality and Uniform Graphene Films on Copper Foils

Preparation of Ultra-Smooth Cu Surface for High-Quality Graphene Synthesis

Surface Engineering of Copper Foils for Growing Centimeter-Sized Single-Crystalline Graphene.

Defect-like Structures of Graphene on Copper Foils for Strain Relief Investigated by High-Resolution Scanning Tunneling Microscopy.

Stacking Relations and Substrate Interaction of Graphene on Copper Foil

The Atomic-scale Growth of Large-Area Monolayer Graphene on Single-Crystal Copper Substrates

A facile method to observe graphene growth on copper foil

Atomic Resolution of Nitrogen-Doped Graphene on Cu Foils.

Preparation of meter-scale Cu foils with decimeter grains and the use for the synthesis of graphene films

Elucidation of heterogeneous graphene nucleation and growth through Cu surface engineering

Surface Monocrystallization of Copper Foil for Fast Growth of Large Single‐Crystal Graphene under Free Molecular Flow

Ultrafast epitaxial growth of metre-sized single-crystal graphene on industrial Cu foil

High-Resolution Scanning Tunneling Microscopy Imaging of Mesoscopic Graphene Sheets on an Insulating Surface

Oxidization‐Temperature‐Triggered Rapid Preparation of Large‐Area Single‐Crystal Cu(111) Foil

Towards intrinsically pure graphene grown on copper

Chemical Vapor-Deposited Graphene on Ultraflat Copper Foils for van der Waals Hetero-Assembly.

One-step synthesis of seamless graphene-carbon nanotube heterojunctions by chemical vapor deposition

Single Crystals: Clean Transfer of Large Graphene Single Crystals for High‐Intactness Suspended Membranes and Liquid Cells (adv. Mater. 26/2017)

Uniform wafer-scale synthesis of graphene on evaporated Cu (111) film with quality comparable to exfoliated monolayer