Abstract:Abstract PbZr0.52Ti0.48O3 nanocrystals were synthesized by a hydrothermal method. The effect of NaOH concentration, reaction temperature and time on nucleation and growth of PbZr0.52Ti0.48O3 nanocrystals was investigated. As the 0.05 mol/L PbZr0.52Ti0.48O3 precursors were heated at 200 °C for 21 h with NaOH concentration of 0.5 mol/L, the tetragonal PbZr0.52Ti0.48O3 nanocrystals were formed, and the grain size was more than 20 nm. With increasing the NaOH concentration from 0.5 to 1.5 mol/L, the grain size of PbZr0.52Ti0.48O3 nanocrystals decreased. When the precursors were heated at different temperatures (140 °C to 200 °C) for 21 h with 1.0 mol/L NaOH, single-phase PbZr0.52Ti0.48O3 nanocrystals were obtained at 160 °C to 200 °C. With increasing the reaction temperature from 160 °C to 200 °C, the grains size of PbZr0.52Ti0.48O3 nanocrystals increased from 5 nm to 9 nm. When the precursors were heated at 160 °C in different reaction times from 6 h to 21 h, the evolution from amorphous to crystalline PbZr0.52Ti0.48O3 nanocrystals in correlation with the reaction time was observed. Single crystalline PbZr0.52Ti0.48O3 nanocrystals with narrow size distribution (from 5 nm to 9 nm) were synthesized by controlling the NaOH concentration, reaction temperature and time. The obtained results can find potential application in preparing PbZr0.52Ti0.48O3 thin films on flexible substrates.

Hydrothermal Synthesis of Rod-Like LaOCl Nanoparticles from New Precursors

Low-temperature chemical solution synthesis of dendrite-like La(OH) 3 nanostructures and their thermal conversion to La 2 O 3 nanostructures

Synthesis of Ultrafine Lanthanum Hydroxide Nanorods by A Simple Hydrothermal Process

Synthesis and Characterization of Lanthanum Hydroxide by Hydrothermal Method

Atomically Efficient Synthesis of Self-assembled Monodisperse and Ultrathin Lanthanide Oxychloride Nanoplates

Synthesis of lanthanum oxalate hierarchical micro-particles and nano-tubes

Synthesis of Lanthanum Hydroxide Nanorods in the Media of Reverse Microemulsions

Synthesis of Single-Crystalline Pb(Zr0.52Ti0.48)O-3 Nanocrystals by Hydrothermal Method

Hydrothermal Synthesis and Characterization of Rare Earth Compound Nanoparticles and Nanorods

Direct Syntheses of Mixed Ion and Electronic Conductors La<sub>4</sub>Ni<sub>3</sub>O<sub>10</sub>and La<sub>3</sub>Ni<sub>2</sub>O<sub>7</sub>from Nanosized Coprecipitates

Amine-Assisted Synthesis and Characterization of Lanthanide Hydroxide Nanorods and Derived Oxides

Effect of La-Introduced Manner on the Phase Formation and Morphology of the Hydrothermally Synthesized Pb_(0.70)La_(0.30)TiO_3 Powders

Preparation of nano-sized lanthanum oxide by ultrasonic-homogeneous precipitation method

Controllable Preparation of Monodisperse LaPO_4 Nanorods

Hydrothermally synthesized Pb0.70La0.30TiO3 powders

Electrodeposition of high aspect ratio LaPO 4 and LaPO 4 :Ln 3+ (Ln 3 + =Ce 3+ , Tb 3+ ) nanostructures

H2SO4-assisted hydrothermal preparation of γ-AlOOH nanorods

Low temperature chemical reaction synthesis of single-crystalline Eu(OH)<sub>3</sub> nanorods and their thermal conversion to Eu<sub>2</sub>O<sub>3</sub> nanorods

Systematic Synthesis of Lanthanide Phosphate Nanocrystals

Controlled synthesis of light rare-earth hydroxide nanorods via a simple solution route

A Simple Method to Synthesize Single-Crystalline Lanthanide Orthovanadate Nanorods