Rapid dislocation-mediated solute repartitioning towards strain-aging hardening in a fine-grained dilute magnesium alloy

Zhen-Ming Hua,Min Zha,Zhao-Yuan Meng,Shen-Bao Jin,Gang Sha,Tian-Shuai Wang,Cheng Wang,Hai-Long Jia,Yipeng Gao,Hui-Yuan Wang
DOI: https://doi.org/10.1080/21663831.2021.2009585
2022-01-02
Materials Research Letters
Abstract:Achieving appreciable strain-aging hardening coupling with fine-grain strengthening remains a critical challenge in dilute Mg alloys, as high-temperature solid-solution, utilized to impart high-level solutes for strain-aging, inevitably causes grain coarsening and great strength loss. Herein, we report a rapid dislocation-mediated solute repartitioning behavior upon aging in a low-temperature annealed Mg–1.0Zn–0.45Ca–0.33Sn–0.2Mn (wt.%) alloy. Thereby, appreciable strain-aging hardening (YS increment of ∼30 MPa) coupling with fine-grain (grain size of ∼2.5 µm) strengthening accounts for a high yield strength (∼297 MPa) and ductility (∼20%). It suggests a feasible avenue to develop strong dilute Mg alloys by combining strain-aging hardening and fine-grain strengthening. By manipulating solute distribution while keeping a fine-grain structure, appreciable strain-aging hardening response coupling with fine-grain strengthening guarantees the development of strong dilute Mg alloy.
materials science, multidisciplinary
What problem does this paper attempt to address?