Abstract:High-strength ceramics were prepared from high alumina fly ash (HAFA) and activated alumina as raw materials with magnesia as a sintering additive. The growth kinetics and influence mechanism of secondary mullite whiskers were investigated. Meanwhile, the effects of the Al2O3/SiO2 mass ratio (A/S) and the amount of magnesia on the content and morphology of mullite in the green body were investigated, so as to emphasize the effect of the liquid phase in the sintering process on the growth of secondary mullite whiskers. The results showed that the aspect ratio of secondary mullite whiskers increased significantly after adding activated alumina to increase the A/S ratio of raw materials. When 30 wt% activated alumina was added, the mullite content increased by 5.39%, and the whisker length increased from 1.36 μm to 4.18 μm. The addition of magnesia improved the liquid phase formed during the sintering process and the K value method was used to determine the sintering liquid phase content under various conditions. It was observed that increasing the magnesia level by 1 wt% could raise the liquid phase content by 5–7%. When the total liquid content of the system was 30–40%, the growth activation energy in the diameter direction of the whisker reduced significantly, promoting the growth of secondary mullite whiskers along the C axis. The morphology of mullite gradually developed from fibrous to long columnar crystal, making it combine more densely with the green body matrix. Furthermore, the staggered long columnar mullite crystal structure changes the fracture mode of ceramics from intergranular to transgranular fracture, which fully uses the high mechanical strength of mullite. As a result, the fracture energy and strength of ceramics are significantly improved.

Activated treatment of magnesite for preparing size-controlled Mg2B2O5 whiskers and their microwave dielectric properties

Study on Preparation of MgO Crystal Whisker from Magnesite

Fabrication of Y2O3-doped MgO Refractory Raw Materials Based on Magnesium Hydroxide from Salt-Lake Brine

Preparation and properties of porous MgO based ceramics from magnesite tailings and fused magnesia

Effect of Mg/B ratio and Sr2+ substitution for Mg2+ on the sintering, phase composition and microwave dielectric properties of Mg3B2O6 ceramics

Formation mechanism of whiskers in Al–MgAl2O4–MgO refractories at 1400 °C under N2 atmosphere

Sintering behaviour and microwave dielectric properties of MgO-2B2O3-xwt%BaCu(B2O5)-ywt%H3BO3 ceramics

High sintering and dielectric performance: The improved (Mg, Zn)3B2O6 ceramics with the help of the DFT calculation

Hydrothermal formation and characterization of magnesium oxysulfate whiskers

Preparation, growth mechanism, and application of Mg2B2O5 whiskers: A review

Preparation of Mullite Whiskers from Kaolin Via the Addition of Tribasic Calcium Phosphate

Properties and mechanism of mullite whisker toughened ceramics

Controllable Synthesis of Mg(OH) 2 Whiskers Using 5Mg(OH) 2 ·MgSO 4 ·2H 2 O Whiskers with Tunable Diameter as Precursors

Effect of TiO 2 whiskers on the microstructure and mechanical and dielectric properties of MgO ceramics

Three‐phase borate solid solution with low sintering temperature, high‐quality factor, and low dielectric constant

Hydrothermal formation of magnesium oxysulfate whiskers in the presence of ethylenediaminetetraacetic acid

Effects of the properties of Mg(OH) 2 precursor on the hydrothermal synthesis of magnesium oxysulfate whiskers

Cracking Behavior of Sm2O3 Ceramics and Enhanced Microwave Dielectric Properties with MgO Addition: Insights from Chemical Bond Characteristics and Microstructure

M- S-H formation in MgO-SiO2slurries via wet milling for magnesia based castables

Synthesis, Phase Composition and Modified Microwave Dielectric Properties of Mg2+ Substituted Zn2SiO4 Ceramics with Uniform Microstructure

Preparation and Characterization of Novel 5Mg(OH)2·MgSO4·7H2O Whiskers