AGING PHENOMENA IN MAGNESIUM RICH ALUMINIUM-ZINC-

SEIKI NISHI

DOI: https://doi.org/10.2464/jilm.1953.8_34

1953-01-01

Journal of Japan Institute of Light Metals

Abstract:To study the mechanism of age-hardening of magnesium rich aluminium-zinc-magnesium alloys, the following experiments were performed. AZI alloy (containing 9.98%Al, 0.75%Zn and bal. Mg), AZ2 alloy (containing 2.35%Al 5.72%Zn and bal. Mg) and AZ3 alloy (containing 0.24%Al, 7.79%Zn and bal. Mg) were prepared and the precipitation constituents of these alloys are, respectively, (Al3Mg4 solid solution), T (Al2Zn3 Mg3 solid solution) and ζ (Zn Mg solid solution). They were solution heat-treated at 425°, 360° and 330°, respectively, then quenched into cold water. With these specimens, (1) changes in hardness, electrical resistance and microscopic structures during aging at room temperature, 100°, 150°, 200° and 250° were studied and also (2) changes in hardness, electrical resistance, thermal expansion and microscopic structures during heating from room temperature to 300° at the heating velocity of 1°C per min., were measured.The results were as follow: (1) In natural aging, AZ2 and AZ3 were hardened to some extent but in the case of AZ1 its hardness increase was less. (2) As to the hardness when quenched, that of AZ1 was the highest (Rockwell-F 72)and those of AZ2 and AZ3 were Rockwell hardness F61. The increments of hardness of these alloys by aging were almost equal, but softening tendency caused by over-aging was considerably remarkable at AZ2, and AZ3 and, at AZ, not so marked. (3) At every aging temperature, experimented, the incubation period of hardening of AZ2, whose precipitation constituent is ternary intermetallic compound (T) phase, was the shortest and that of AZ1 the longest. The hardening velocity of initial hardening period of AZ2 was the highest and that of AZ1 the lowest. In the case of tempering by ascending temperature, AZ3 began hardeningfirst and AZ1 last, (4) These three alloys harden by precipitation of the second phase from super-saturated solid solution, but the effect given by precipitation to crystal lattices depends on the degree of supper-saturation of the solid solution, and the hardening takes place in two stages and this fact is distinct in lower temperature aging. The principal hardening of AZ1 was the first hardening stage and those of AZ2 and AZ3 were the second one. (5) The type of precipitation of AZ1 alloy belongs to "discontinuous type, " that is, at first, precipitation takes place along grain boundaries and, after this stage finished, at the remaining parts of grains, but those of AZ2 and AZ3 are "continuous type" ("general precipitation").As one of the factors which causes such different types of precipitation, I propose the difference of diffusion velocity of solute atoms in the super-saturated solid solution.