Study of optical and magnetic properties of Mn-substituted bismuth ferrite thin films

R. Prasannakumara,D. P. Rai,K. Gopalakrishna Naik

DOI: https://doi.org/10.1007/s10854-021-07233-2

2021-10-25

Abstract:The Sol–gel spin-coating method was used to deposit Bismuth Ferrite (BiFeO3) and Mn-substituted BiFeO3 (BiFe1−xMnxO3) thin films on glass substrates. The powder XRD data of the grown BiFeO3 thin films indicated a distorted rhombohedral structure. The powder XRD data of the Mn-substituted BiFeO3 thin films indicate the change of crystal structure from distorted rhombohedral to orthorhombic. FESEM and AFM imaging were used to investigate the surface morphology and topography of the grown thin film samples. The UV–visible absorption studies BiFe1−xMnxO3 thin films that show an increase in optical absorption as the Mn substitution increases in the films, and correspondingly, the UV–visible transmittance of the films decreases with an increase in Mn substitution. The optical bandgap obtained from the UV–visible optical absorption of spectra of the BiFe1−xMnxO3 thin films was found to decrease with an increase in Mn substitution. The FTIR absorption band with maximum absorption around 550 cm−1 indicates the formation of BiFe1−xMnxO3. The Raman spectra of the samples recorded over the range of 200–800 cm−1 confirm the formation of BiFe1−xMnxO3. The magnetic hysteresis (M–H) loops of the BiFe1−xMnxO3 thin films were measured with a magnetic field up to 70 kOe at 10 K and room temperature using a SQUID magnetometer. The room temperature M–H loops of the sample show weak ferromagnetism and the 10 K M–H loops show superparamagnetic behavior.

engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied