Abstract:0.67BiFeO3-0.33BaTiO3 multiferroic ceramics doped with x mol% MnO2 (x = 2–10) were synthesized by solid-state reaction. The formation of a perovskite phase with rhombohedral symmetry was confirmed by X-ray diffraction (XRD). The average grain sizes were reduced from 0.80 μm to 0.50 μm as increasing the Mn-doped levels. Single crystalline nature of the grains was revealed by high-resolution transmission electron microscopy (HRTEM) images and electron diffraction patterns. Polar nano-sized ferroelectric domains with an average size of 9 nm randomly distributed in the ceramic samples were revealed by TEM images. Ferroelectric domain lamellae (71° ferroelectric domains) with an average width of 5 nm were also observed. Vibrational modes were examined by Raman spectra, where only four Raman peaks at 272 cm−1 (E-4 mode), 496 cm−1 (A1-4 mode), 639 cm−1, and 1338 cm−1 were observed. The blue shifts in the E-4 and A1-4 Raman mode frequencies were interpreted by a spring oscillator model. The dieletric constants of the present ceramics as a function of the Mn-doped levels exhibited a V-typed curve. They were in the range of 350–700 measured at 103 Hz, and the corresponding dielectric losses were in range of 0.43–0.96, approaching to 0.09 at 106 Hz.

Multiferroic And Magnetoelectric Properties Of Bi(1-X)Baxfe(1-X)Mn(X)O(3) System

Multiferroic and magnetoelectric properties of Bi<sub>1−<i>x</i></sub>Ba<sub><i>x</i></sub>Fe<sub>1−<i>x</i></sub>Mn<sub><i>x</i></sub>O<sub>3</sub>system

Room Temperature Ferroelectric, Ferromagnetic and Magnetoelectric Properties of Ba-Doped Bifeo3 Thin Films

Evolution of structure, magnetism and ferroelectricity in the (1-x)BiFeO3-xBa0.5Sr0.5MnO3(0≤x≤1) solid solutions

Magnetic and Electrical Properties of Bi0.8Ca0.2Fe1−xMnxO3 (0≤X≤0.5)

Large Magneto-Electric Effects In Hexagonal La0.7ba0.3mno3-Batio3 Solid Solutions And Magneto-Electric Coupling Mechanism Discussion

Room temperature multiferrocity and magnetodielectric properties of ternary (1-x) (0.94Bi<sub>0.5</sub>Na<sub>0.5</sub>TiO<sub>3</sub>-0.06BaTiO<sub>3</sub>)-xBiFeO<sub>3</sub> (0 ≤x≤ 0.9) solid solutions

Magnetodielectric Properties of Bi4ndti3fe0.7co0.3o15 Multiferroic System

Room Temperature Multiferrocity And Magnetodielectric Properties Of Ternary (1-X) (0.94bi(0.5)Na(0.5)Tio(3)-0.06batio(3))-Xbifeo(3) (0 <= X <= 0.9) Solid Solutions

Multiferroicity in single phase Bi0.9Ba0.1Fe0.85Mn0.15O3 ceramic

The magnetoelectric coupling in rhombohedral–tetragonal phases coexisted Bi0.84Ba0.20FeO3

Structural, Spectroscopic, and Dielectric Characterizations of Mn-doped 0.67bifeo 3 -0.33Batio 3 Multiferroic Ceramics

The Multiferroic Properties of (bi(0.9)ba(0.1))(fe(0.95)mn(0.05))o(3) Films

Structural, Magnetic and Ferroelectric Properties of Sm and Mn Co-Substituted BiFeO3 Ceramics with Composition Near the Morphotropic Phase Boundary

Ferroelectric and Ferromagnetic Properties of Mn-doped 0.7bifeo3–0.3batio3 Solid Solution

Structural Transformation and Multiferroic Properties of Single-Phase Bi0.89Tb0.11Fe1−xMnxO3 Thin Films

Synthesis, Microstructure, and Dielectric Properties of Mn-Doped 0.33BaTiO<sub>3</sub>-0.67BiFeO<sub>3</sub> Multiferroic Solid Solutions

Effect of Mn Substitution on Microstructures, Dielectric and Magnetic Properties of BiFeO<sub>3</sub> Ceramics

Multiferroic Properties in Ba0.93Bi0.07Ti1−xMnxO3 Ceramics

The Multiferroic Properties of BiFe0.5Mn0.5O3 and BiFeO3/BiMnO3 Superlattice Films

Effect of Mn Substitution on Microstructures, Dielectric and Magnetic Properties of BiFeO3 Ceramics