Synthesis and study on structural, magnetic, dielectric properties and impedance spectroscopy of nanosized Mn-doped γ-Fe2O3 for multifunctional applications
R. E. El-Shater,S. T. Assar,Basem E. Keshta,Ali H. Gemeay,H. H. El-Bahnasawy,E. K. Abdel-Khalek,F. Fakhry
DOI: https://doi.org/10.1007/s10971-024-06579-3
2024-11-04
Journal of Sol-Gel Science and Technology
Abstract:Nano structured samples of γ-Mn x Fe 2- x O 3 (0 ≤ x ≤ 1.0, step 0.2) were prepared by a wet-chemical method. The formation of the pure-phase FCC spinel structure of the samples has been confirmed by x-ray diffraction and Fourier Transform Infrared spectroscopy, where their crystallite size increases from 12 to 28 nm by adding Mn 3+ ions. The high-resolution transmission electron microscopy images show spherical-shaped agglomerated nanoparticles with uniform size, confirming the nanostructure of the samples. The X-ray photoelectron spectroscopy and Mössbauer results confirm the existence of Fe 3+ and Mn 3+ ions and the disappearance of the Fe 2+ and Mn 2+ ions in the cubic structure of the γ-Mn x Fe 2- x O 3 . The Brunauer–Emmett–Teller specific surface area of the samples ranges from 36 to 79 m 2 /g, where the sample of x = 0.2 has the largest value. The sigmoid-shaped hysteresis loops reflect the soft magnetic nature of the samples. As the Mn 3+ ion addition increases, the M s and M r increase up to the sample of x = 0.4, then decrease again. The H c , which has lower values, increases as the crystallite size increases, manifesting the single-domain nature of the particles and approaching the superparamagnetic limits. The composition dependence of σ dc , σʹ ac , εʹ , εʺ , and tanδ is dependent on grain size, specific surface area, and cation distribution.
materials science, ceramics