Abstract:A long-standing conflict concerning metastable β-titanium (Ti) alloys is that high strength can be achieved through precipitation strengthening of α-phase while plasticity is largely compromised and even lost completely. Such strength-plasticity trade-off severely limits their structural applications. Here, an attempt to address the issue has been made in Ti–6Cr–5Mo–5V–4Al (Ti6554) high-strength metastable β-Ti alloy. Heterogeneous β-structure is architected by partial static recrystallization (SRX) through properly manipulating solution treatment in the hot-rolled bars. The resulting microstructure is composed of the recrystallized ‘new’ equiaxed β-grains (βe) and the remnant elongated β-fibers (βf). This β-morphology dramatically affects the subsequent αs-precipitation behavior during the aging process. αs-precipitation is rather uniform throughout βf-grains because the pre-existing dislocations left by hot rolling provide copious nucleation sites. However, αGB-films are preferentially formed along βe-grain boundaries, which leads to a boundary-affect zone (BAZ) and thereby renders αs-precipitation in a size gradient from β-grain boundaries to grain interiors. As a result, an ultra-high strength of ∼1700 MPa is achieved whilst the ductility can be up to be 5% in the β-hetero aged samples, which is superior to the β-homo aged siblings that have the same strength level but fully succumb to macroscopic brittleness. The enhanced plasticity in the β-hetero aged samples originates from much better deformation compatibility conferred by the aged βf-grains. However, the soft feature of BAZ around βe-grain boundaries in the β-homo aged samples causes strain localization, which eventually induces intergranular brittle fracture. These findings provide an effective strategy for enhancing plasticity of high-strength metastable β-Ti alloys by structural design, where homogeneous αs-precipitates can be easily constructed by combining conventional thermomechanical processing and heat treatment.

Strength and ductility optimization of laser additive manufactured metastable β titanium alloy by tuning α phase by post heat treatment

Effect of Solution and Aging Treatments Parameters on Microstructure and Mechanical Properties of Laser Additive Manufactured Ti-10V-2Fe-3Al Metastable β

Heat-treatment induced microstructural evolution and enhanced mechanical property of selective laser melted near β Ti-5Al-5Mo-5 V-3Cr-1Zr alloy

Laser additive manufacturing of new α+β titanium alloy with high strength and ductility

Achieving Enhanced Tensile Strength-Ductility Synergy Through Phase Modulation in Additively Manufactured Titanium Alloys

Unveiling the impact of heat treatment on powder-metallurgy α+β titanium alloy for achieving a superior strength-ductility combination

Electron Beam Welding and Post Heat Treatment of a New Near-Beta High-Strength Ti-4Al-5Mo-5V-5Cr-1Nb Alloy

Microstructure and mechanical properties of laser additive manufactured novel titanium alloy after heat treatment

Additive manufacturing of titanium alloys with enhanced strength and uniform ductility via multi-element alloying

The ageing response of direct laser deposited metastable β-Ti alloy, Ti–5Al–5Mo–5V–3Cr

Microstructure and Mechanical Properties of An Ultrahigh-strength Titanium alloy Ti-4.5Al-5Mo-5V-6Cr-1Nb Prepared Using Laser Directed Energy Deposition and Forging: A Comparative Study

Achieving high strength-ductility synergy in a hierarchical structured metastable β-titanium alloy using through-transus forging

Balance of strength and ductility for laser directed energy deposited Ta-containing Ti6Al4V via solution and aging treatment

Homogeneous α-precipitation and enhanced plasticity in Ti–6Cr–5Mo–5V–4Al high-strength metastable titanium alloy with heterogenous β-structure

Simultaneous improvement of strength and elongation of laser melting deposited Ti-6Al-4V titanium alloy through three-stage heat treatment

Obtaining heterogeneous α laths in selective laser melted Ti–5Al–5Mo–5V–1Cr–1Fe alloy with high strength and ductility

Effect of Post-Heat Treatment on Ti2AlNb-based Alloy Fabricated by Twin-Wire Alternating Dual-Electron Beam Additive Manufacturing Technology

Preparation of Multiscale α Phase by Heat Treatments and Its Effect on Tensile Properties in Metastable β Titanium Alloy Sheet

Microstructure evolution and mechanical property of a new multi-component β titanium alloy with ultrahigh strength above 1350 MPa

Combination of multiple strengthening mechanisms facilitates excellent strength-ductility balance in metastable β titanium alloy

Effect of Heat Treatment on the Microstructure and Mechanical Properties of Additive Manufactured Ti-6.5Al-2Zr-1Mo-1V Alloy