Abstract:Two compositions Ce0.50Zr0.39La0.04Y0.07O2−δ and Ce0.25Zr0.65La0.04Y0.06O2−δ based on ceria-zirconia solid solutions were prepared as nanopowders using a continuous hydrothermal flow synthesis reactor, followed by either freeze-drying or hotplate-drying of the slurry. Each dried nanopowder was then subjected to 10h heat-treatment at 1000°C, 1100°C or 1200°C in air (to simulate accelerated ageing). The reducibility and hydrogen consumption of the oxidised samples were measured using temperature programmed reduction (TPR) up to 1000°C. The effects of composition, drying method and heat-treatment temperature were evaluated on the TPR profiles of the materials. The powders were further investigated using a range of analytical methods including UV/Vis spectroscopy (which yielded colour data), Raman spectroscopy, powder X-ray diffraction, BET surface area measurements and X-ray photoelectron spectroscopy (XPS). Chemometric methods were used to investigate relationships between the spectroscopic and total oxygen storage capacity (OSC) data. Principal component analysis (PCA) was used to provide a simple interpretation of the effects of various synthesis and treatment parameters on Raman spectra. Principal component regression (PCR) was used to build regression models relating the Raman spectra and the temperature of hydrogen consumption peak at several set temperatures in the TPR. The total hydrogen consumption of the materials was generally high, while the drying and heat-treatment conditions appeared to have a significant effect on the final properties of the resulting powders, such as the surface area and total oxygen storage capacity.

Phase stability and rapid consolidation of hydroxyapatite–zirconia nano-coprecipitates made using continuous hydrothermal flow synthesis

High-Throughput Continuous Hydrothermal Synthesis of an Entire Nanoceramic Phase Diagram

Continuous Hydrothermal Flow Syntheses of Nanosized Energy Materials Used in Solid Oxide Fuel Cells

Micro-hydrothermal reactions mediated grain growth during spark plasma sintering of a carbonate-containing hydroxyapatite nanopowder

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Thermal Stability and Mechanical Properties of Zirconia–hydroxyapatite Composites

Spark Plasma Sintered Hydroxyapatite-Yttria Stabilized Zirconia Composites

Physico-mechanical and morphological features of zirconia substituted hydroxyapatite nano crystals

Synthesis of Monolithic Zirconia with Macroporous Bicontinuous Structure Via Epoxide-Driven Sol–gel Process Accompanied by Phase Separation

Supercritical Hydrothermal Synthesis of Nano-Zirconia: Reaction Path and Crystallization Mechanisms of Different Precursors

Characterization on Ti35Nb7Zr Based Hydroxyapatite Composites Prepared Via Rapid Sintering for Biomedical Applications

Crystallization Characteristics and Thermal Stability of Fluor-Hydroxyapatite Composites with Zirconia

Rapid processes for the production of nanocrystal yttria-stabilized tetragonal zirconia polycrystalline ceramics: ultrasonic spray pyrolysis synthesis and high-frequency induction sintering

Nano-Hydroxyapatite-Zirconia Ceramics Sintered by Spark Plasma Sintering

Spark Plasma Sintered Hydroxyapatite-Yttria Stablized Zirconia Composites

Fabrication and properties of a stable and porous YSZ/nano-HA structure by binder jetting processes

Laminated and Functionally Graded Hydroxyapatite/yttria Stabilized Tetragonal Zirconia Composites Fabricated by Spark Plasma Sintering.

In-situ synchrotron X-ray diffraction of hydroxyapatite-zirconia composite during conventional and flash sintering

High-throughput continuous hydrothermal synthesis of nanomaterials (part II): unveiling the as-prepared CexZryYzO2-δ phase diagram

Transparent Hydroxyapatite Ceramics with Nanograin Structure Prepared by High Pressure Spark Plasma Sintering at the Minimized Sintering Temperature

Hydrothermal synthesis of (ZrO2)0.86(Sm 2O3)0.14 nano-powders and electrical properties of its sinter