Novel testing method for thixotropy of paste slurry with respect to influencing factors and rheological parameters

Youzhi Zhang,Deqing Gan,Zhenlin Xue,Hongjian Lu

DOI: https://doi.org/10.1016/j.apt.2021.10.031

IF: 4.969

2021-12-01

Advanced Powder Technology

Abstract:Paste slurry exhibits significant thixotropy, which has a significant influence on the slurry pipeline transportation resistance. This paper proposes a novel test method for the thixotropy of paste slurry, which can ensure that the slurry reaches flow equilibrium during the test. Accordingly, the influences of the solid mass concentration, cement-to-tailings ratio, and temperature on thixotropy were studied by employing a control variable method, and the influences of the above three factors on the stress overshoot and rheological parameters were evaluated. The results revealed that the solid mass concentration and temperature have significant influence on the thixotropy. Moreover, with an increase in the solid mass concentration, the time required for the slurry to reach flow equilibrium decreases. The cement content and temperature are proportional to the significance of the stress overshoot, and the change in dynamic yield stress can be considered an indicator for the effective quantification of thixotropy. In the continuous shearing cycles, the maximum apparent viscosity at the start of shearing significantly decreases on the time axis. The solid mass concentration has a significant influence on the minimum apparent viscosity in the slurry flow process, whereas the cement-to-tailings ratio and temperature have no significant influences.

engineering, chemical