Effect of the Material and Sliding Rate of the Counterface on the Tribotechnical Properties of a CM(Ti–Mo–BN)–Steel Friction Pair
A. G. Kostornov,O. I. Fushchich,T. M. Chevychelova,V. T. Varchenko,O. D. Kostenko
DOI: https://doi.org/10.1007/s11106-015-9732-5
2015-11-01
Powder Metallurgy and Metal Ceramics
Abstract:The effect of the material and sliding rate (1, 2, 4, 6, and 15 m/sec) of the counterface on the tribological characteristics of a (composite Ti–Mo–BN)–counterface (steels 45, 65G, ShKh15, 40Kh, and Kh18N9T, nitrided titanium, and BrO10 bronze) friction pairs in dry friction in air under a pressure of 0.8 MPa is investigated. It is established that, under these friction conditions, the composite in pair with BrO10 bronze is ineffective. During friction of the composite in pairs with steels 45, 65G, ShKh15, 40Kh, and Kh18N9T, an increase in the sliding rate from 1 to 6 m/sec results in an increase of the friction coefficient, linear wear of the friction pairs, mass loss of the composite and counterface, whereas the temperature of the friction surface increases. The highest temperature of the friction surface of the composite is reached in pair with steel 45. The temperature, sliding rate, and pressure applied lead to the synthesis of a secondary film (on the surface of the composite) of such a phase composition and structure that provide (in pair with steel 45) higher tribological characteristics of the composite than those in pairs with the other steels. At all sliding rates of the counterface, the tribological properties of the friction pairs depend not only on the properties of the composite material (chemical and phase composition, structure, and mechanical characteristics), but also on the same properties of the counterface material.
metallurgy & metallurgical engineering,materials science, ceramics