Abstract:A MoNx coating serves as an effective wear protection layer and is crucial for the investigation of its tribological characteristics at various temperatures. This study examined the tribological characteristics of MoNx coatings that were deposited through high-power pulsed magnetron sputtering (HiPIMS) in an Ar/N2 environment with varying N2 partial pressures. The microstructures and mechanical properties of the coatings were elucidated using scanning electron microscopy, grazing-incidence-angle X-ray diffraction, energy-dispersive spectroscopy, and nanoindentation. The dry friction performances of the coatings at different heating temperatures were studied using a ball-on-disk tribometer. The MoNx coating produced by HiPIMS was composed primarily of fcc−Mo2N and featured a fine, dense column crystal with a maximum hardness of 28.8 GPa. The MoNx coatings exhibited excellent lubrication and wear reduction properties at room temperature (RT). The dry friction performances of the MoNx coatings at elevated temperatures were expected to depend on the growth of the MoO3 tribolayer. At relatively low temperatures (300 °C and 400 °C), the MoO3 tribolayer grew slowly and was not enough to provide good lubrication, causing increases in the dry friction of the coatings. However, the δ−MoN phase formed in the MoNx coating deposited at a high N2 partial pressure could facilitate the formation of MoO3 and thus decreased the friction coefficient at 400 °C. At the relatively high heating temperature of 500 °C, however, the MoO3 tribolayer grew so rapidly that the oxide layer became thick, resulting in an increase in the wear rate. It is believed that tuning the growth rate of MoO3 via optimizing the composition and structure of the MoNx coatings might be a useful way to improve the dry friction at various elevated temperatures.

Influence of copper on the compositions, microstructure and room and elevated temperature tribological properties of the molybdenum nitride film

High temperature tribological behaviors and wear mechanisms of NiAl-MoO3/CuO composite coatings

Study on the tribological properties of MoB/Cu laminated composite materials fabricated by hot-pressing process

The effect of molybdenum content on microstructure, mechanical, tribological and corrosion behavior of Zr-Mo-N composite films

Effect of CaF2 surface layers on the friction behavior of copper-based composite

Investigation of the elevated temperature tribological property and wear mechanism of Fe‐15Cu‐0.8C materials containing Mo‐coated MoS2 powders

Influence of Cu Content Variation on the Tribological Properties of Ni60CuMo with Sandwich-Structured Composite Coatings by Laser Cladding

Influence of structure parameters on the tribological properties of MoB/Cu laminated composites

High-temperature Tribological Properties of the Novel NiCr(MoNb)x-Ag Self-Lubricating Composite Films

Suppressed MoO3/FeMoO4 formation in molybdenum dialkyl-dithiocarbamate-derived tribofilms on nitrogen-incorporated Al-Mg-Ti-B coatings

Improved tribological performance of nickel based high temperature lubricating composites with addition of metallic oxides

High-Temperature Friction and Wear Behavior of Nickel-Alloy Matrix Composites with the Addition of Molybdate

Microstructure and wear characteristics of in-situ micro/nanoscale niobium carbide reinforced copper composites fabricated through powder metallurgy

Dry Friction Performances of MoNx Coatings Deposited by High−Power Pulsed Magnetron Sputtering

Effect of Cu content on high-temperature tribological properties and oxidation behavior of Al-Ti-V-Cu-N coatings deposited by HIPIMS

Preparation and tribological properties of NiCr–Mo–Ag–O/Mo–V–Ag–O bilayer film at RT-1000 °C

Effect of Cr addition on oxidation and tribological properties of MoB 2-z films by magnetron sputtering

Friction and Wear Characteristics of Electrodeposited Ni‐based Metallic Coatings on Cu‐substrate under High‐Temperature Conditions

Tribological Performance of Magnetron Sputtered Molybdenum Nitride Film on N-Permeated Piston Ring

Tribological Behavior of Cu-Modified Polymer-derived SiBCN Ceramics at Elevated Temperature

Microstructure, Mechanical and Tribological Properties of Mo-V-N Films by Reactive Magnetron Sputtering