Abstract:Electroless nickel composite coatings have the potential for high-temperature tribological applications, and a combination of high wear resistance and low friction factor is one of the desirable solutions but still a tricky problem. The addition of self-lubricating WS2 and hard Si3N4 nanoparticles to the Ni-P coatings is expected to obtain good high-temperature tribological performance. In this work, Ni-P-Si3N4-WS2 composite coatings with various contents of WS2 nanoparticles were prepared using electroless plating and subsequently annealed at 400 °C in an inert atmosphere. The tribological properties of the coatings were evaluated using a ball-on-disc wear instrument at operating temperatures from 25 to 600 °C. The microstructure, chemical composition, and surface morphology of the coatings were characterized by X-ray diffractometry (XRD), energy disperse spectroscopy (EDS), and scanning electron microscopy (SEM). Upon increasing the WS2 dosage in the bath, the WS2 content in the coating increased and the micro-hardness of the as-plated coating increased from 539 to 717 HV. After heat treatment, the coating underwent a crystallization process, and the hardness increased from 878 to 1094 HV. The main wear mechanism of the coating changed from adhesive wear in the as-plated state to abrasive wear in the annealed state. The annealed Ni-P-Si3N4-WS2 coating with a WS2 dosage of 2.5 g/L in the bath exhibited excellent mechanical properties, with a hardness of 10.9 GPa, a friction coefficient of ~0.51, and a wear rate of 8.4 × 10−15 m3N−1×m−1 at room temperature, and maintained optimal performance at high temperatures. At operating temperatures of 200, 400, and 600 °C, the form of wear was adhesive wear for coatings with a WS2 dosage < 1.5 g/L and abrasive wear for coatings with a WS2 dosage ≥ 1.5 g/L. The synergism of WS2 and Si3N4 particles refined the grains of the Ni-P matrix in as-plated coatings and obviously reduced the friction coefficient of friction pairs in annealed coatings at all operating temperatures.

Friction and Wear Characteristics of Electrodeposited Ni‐based Metallic Coatings on Cu‐substrate under High‐Temperature Conditions

Tribological Behavior of Atmospheric Plasma-Sprayed Cu-Ni Coatings

Preparation and properties of Ni-P/Bi self-lubricating composite coating on copper alloys

Influence of Cu Content Variation on the Tribological Properties of Ni60CuMo with Sandwich-Structured Composite Coatings by Laser Cladding

High Temperature Tribological Behavior of Electroless Plating Ni-P-Si3N4-WS2 Composite Coatings

Corrosion and Wear Resistance of HVOF-Sprayed Ni-Cr-Co Multi-principal Element Alloy Coating on Copper Plate

The effect of advanced electrodeposited Ni-P-Cu coatings obtained with scrap cu plates on the tribological performance of Al powder metallurgy products

Effects of Nickel on the Oxide/Metal Interface Morphology and Oxidation Rate During High-Temperature Oxidation of Fe–Cu–Ni Alloys

Friction and wear behaviors of electrodeposited Ni-P-CNTs composite coatings on Al-alloy substrate

Effect of Cu content on high-temperature tribological properties and oxidation behavior of Al-Ti-V-Cu-N coatings deposited by HIPIMS

Preparation of Ni-Cnt Composite Coatings on Aluminum Substrate and Its Friction and Wear Behavior

Microstructure and tribological properties of electrodeposited Ni–Co alloy deposits

High temperature tribological behaviors and wear mechanisms of NiAl-MoO3/CuO composite coatings

Preparation of the electroless Ni–P and Ni–Cu–P coatings on engine cylinder and their tribological behaviors under bio-oil lubricated conditions

Copper–Nickel Alloy Friction Surfaced Coating on Steel Substrates for Marine Applications

Elevated temperature tribological assessment of Ni-based cermet self-lubricating coatings deposited by cold spray

Oxidation issues during heat treatment and effect on the tribo-mechanical performance of electroless Ni-P–Cu deposits

Wear and Corrosion Properties of Crystalline Ni-W Alloy Coatings Prepared by Electrodeposition

Tribo-induced surface structure of Nickel-based superalloy at elevated temperature

Effects of Temperature and Normal Load on Tribological Behavior of Nickel-Based High Temperature Self-Lubricating Wear-Resistant Composite Coating

Tribological and corrosion performance of duplex electrodeposited Ni-P/Ni-W-P coatings