Alloying behavior of W and Mo in the as-cast dual-phase FeNiCrAl multi-component alloys
Jianbin Wang,Zhijun Wang,Xinbo Shi,Xiaoming Liu,Yuhao Jia,Junjie Li,Feng He,Jincheng Wang
DOI: https://doi.org/10.1016/j.jallcom.2023.169951
IF: 6.2
2023-04-07
Journal of Alloys and Compounds
Abstract:The W and Mo are in the same groups of periodic table and are usually used as solid solution elements. In this investigation, the minor alloying behaviors of W and Mo in Fe 37 Ni 36 Al 17 Cr 10 alloy were explored. The addition does not change the casting microstructure greatly, with dendrite region of FCC + B2 and inter-dendrite region of FCC phase. For tensile properties at ambient temperature, as-cast Fe 36 Ni 36 Al 17 Cr 10 Mo 1 alloy exhibited higher yield strength and fracture strength compared with Fe 37 Ni 36 Al 17 Cr 10 alloy. Then, dual-phase alloys with Mo content of 2 and 3 at% were further designed and carefully studied. It is found that a nano-scale structure occurred in as-cast Fe 35 Ni 36 Al 17 Cr 10 Mo 2 alloy, where a large number of spherical BCC precipitates are distributed in the dendrite region of B2 phase. Meanwhile a mixture of irregular B2 phase and FCC phase is contributed to the inter-dendrite area. The Fe 35 Ni 36 Al 17 Cr 10 Mo 2 alloy exhibited the most excellent and comprehensive mechanical properties due to the fine structure and its high work hardening ability. The yield strength, ultimate tensile strength and fracture elongation of as-cast Fe 35 Ni 36 Al 17 Cr 10 Mo 2 alloy are 863 ± 20 MPa, 1285 ± 17 MPa and 16.0 ± 1.0 %, respectively, which is higher than the most of reported dual-phase as-cast FeNiCrAl multi-component alloys.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering