Abstract:In this research, the influence of short-term natural re-aging after T351 temper on the microstructural evolution and mechanical behavior of AA2024 aluminum alloy was investigated. Grain growth occurred in the microstructures of the natural re-aged sample and a large number of Al7Cu2Fe particles were located inside the alpha grains. At the re-aging time of 1440 min, the peaks of XRD were shifted strongly to the right due to the formation of θ'', S″, θ', and S'. The results revealed that the precipitation rate was high in the AA2024 alloy during natural aging. With increasing the re-aging time, texture parameters remained almost unchanged. The hardness increased slowly within the first 60 min, then enhanced rapidly between 60 and 2880 min, and finally became stable at around 139 HV between 2880 and 11520 min. When the natural re-aging time increased from 240 to 2880 min, the strengthening trended speed up, viz, the yield strength increased from 226.6 to 357.3 MPa, and the ultimate tensile strength enhanced from 452.2 to 535.5 MPa. Compared to the as-received sample (T351 temper), the ultimate tensile strength of the re-aged sheet improved from 455.5 to 535.5 MPa, the ductility remained unchanged, and the hardness increased from 128.8 to 138.2 HV, which was owing to the acceleration of the precipitation caused by the presence of high-content Al7Cu2Fe particles in the interior of the alpha-aluminum grains in the natural re-aged sample. It was found that the Portevin-Le Chatelier instability of AA2024 alloy was effectively postponed after natural re-aging. With increasing the natural re-aging time, the strain hardening rate of the AA2024 sheet increased. The strengthening of the natural re-aged sample for 1440 and 2880 min was a result of a synergistic effect of precipitation hardening due to the formation of θ'', S″, θ', and S' phases, elimination of Portevin Le-Chatelier instability, and highly efficient load transfer from alpha-aluminum to Al7Cu2Fe. Finally, to use the A2024 alloy produced by natural re-aging for 1440 or 2880 min, two methods were proposed.

Thermo-Kinetic Simulation of the Yield Strength Evolution of AA7075 during Natural Aging

Atomic-scale study on the precipitation behavior of an Al-Zn-Mg-Cu alloy during isochronal aging

Natural Aging Behaviors and Mechanisms of 7050 and 5A90 Al Alloys: A Comparative Study

Experimental investigation and modelling of yield strength and work hardening behaviour of artificially aged Al-Cu-Li alloy

Microstructural Influences Caused by Different Aging Strategies on the Strain-Dependent Damping of the High-Strength Aluminum Alloy AA7075

Evading the strength-ductility trade-off dilemma in AA2024 alloy by short-term natural re-aging after T351 temper

Effects of different initial states on dynamic tensile properties and microstructure of 7075 aluminum alloy

Modeling the Precipitation Kinetics and Tensile Properties in Al-7si-Mg Cast Aluminum Alloys

Modeling Microstructure and Yield Strength during Solidification and Heat Treatment Process in Al-7Si-Mg Cast Aluminum Alloys

Experimental and Simulation Study for the Influence of Thermal Pre-Deformation on Subsequent Aging Precipitation Kinetics of Al-Zn-Mg-Cu Alloy

Mechanical behaviors of metallic alloys dominated by thermo-kinetic synergistic effects upon materials processing

Modelling the Effect of Room Temperature Storage and Deformation on the Age-hardening Behaviour of Al-Mg-Si alloys

Effect of Aging Treatment on Microstructure and Mechanical Properties of As-Extruded AA6063 Aluminum Alloy

Aging behavior of an Al–Cu–Mg alloy

Integrated microstructural simulations and mechanical property predictions for age-precipitated Al–Mg–Si alloys

Multi-scale Simulation of Al–Cu–Cd Alloy for Yield Strength Prediction of Large Components in Quenching-Aging Process

Constitutive modelling of coupled creep deformation and age hardening behavior of aluminum alloys under various thermal and mechanical loadings

Modeling the Age-Hardening Process of Aluminum Alloys Containing the Prolate/Oblate Shape Precipitates

Natural and Artificial Aging Effects on the Deformation Behaviors of Al-Mg-Zn Alloy Sheets

The Influence of Creep Ageing on the Hardening Behavior and Microstructure of 7050 Aluminum Alloy

Hot tensile deformation behavior and microstructure evolution of 7075 aluminum alloy sheet