Surface Tension of Cu-Ti Alloys and Wettability in a Liquid Alloy–Refractory Material-Gaseous Phase System
Katarzyna Nowinska,Grzegorz Siwiec,Tomasz Matula,Alphonce Wikedzi,Beata Oleksiak,Jaroslaw Piatkowski,Tomasz Merder,Mariola Saternus
DOI: https://doi.org/10.3390/ma17194786
IF: 3.4
2024-09-29
Materials
Abstract:The study involved measurements of surface tension of liquid binary copper-titanium alloys with respect to their chemical composition and temperature as well as investigations of the liquid alloy–refractory material-gaseous phase system wettability using usual refractory materials, i.e., graphite, aluminum oxide and magnesium oxide. The experiments were performed with the use of the sessile drop method and a high-temperature microscope coupled with a camera and a computer. The aim of this study was to determine the influence of titanium content in the Cu-Ti alloy on the surface tension and contact angle at the interface between the liquid alloy and the refractory material. The influence of temperature on these parameters was also examined. The tests were carried out for copper-titanium alloys with a maximum content of 1.5% wt. Ti, in the temperature range of 1373 to 1573 K. The test results indicate that as the titanium content in the alloy increases, its surface tension increases slightly. However, an increase in temperature causes a decrease in the surface tension of the alloys. In the case of an alloy containing 1.5% wt. Ti, surface tension at a temperature of 1373 K reaches 1351 mN∙m−1, and at a temperature of 1573 K, it decreases to 1315 mN∙m−1. As the temperature and titanium content in the alloy increase, a decrease in the contact angle is observed. The highest values of contact angles were recorded in the case of contact of the liquid alloy with graphite. For an alloy containing 0.1% wt. Ti at a temperature of 1373 K, the contact angle reaches 132°, while at a temperature of 1573 K, it decreases to 128°. For an alloy containing 1.5% wt. Ti, the values of contact angles are 100° and 96°, respectively. However, the contact angles have the lowest values for magnesium oxide. In the case of a temperature of 1573 K and an alloy containing 1.5% wt. Ti, the contact angle reaches 49°. Such a significant impact of titanium content on the contact angles may be due to its high affinity for oxygen (contact with a substrate made of Al2O3 and MgO and its reactivity with carbon (contact with graphite).
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering