Abstract:The polyoxymethylene (POM) fiber was melt spun by use of different commercial grades of POM resin, and the effect of post-drawing on mechanical properties and microstructures was investigated extensively. The fiber obtained from the POM resin with a higher melt flow index (MFI) exhibits a better hot-drawing capability and also achieves a greater ultimate draw ratio. The mechanical evaluation reveals that the tensile strength and elastic modulus of POM fiber are improved significantly after post-drawing compared to the as-spun fibers. Although the greater draw ratios result in higher mechanical strength and modulus for the POM fiber, the fiber obtained from the POM resin with an MFI of 13.0 g/10 min achieves the optimal mechanical performance at the ultimate draw ratio. The morphologic and structural developments of POM fiber were studied by scanning electronic microscopy and X-ray powder diffraction. The results indicate that the POM fiber spun by the resin with an MFI of 13.0 g/10 min has a smooth lateral surface and a compact cross section after post-drawing. The fiber samples spun by the POM resins with low MFIs show some hollow disfigurements as well as a rough surface at the ultimate draw ratio, whereas the fiber obtained from the resin with a high MFI of 27.0 g/10 min presents the ununiformity of diameter after post-drawing. The POM fibers achieve a crystalline orientation during the hot-drawing process, which results in a transformation from the spherulitic crystals to the lamellar structure in the drawing direction. The level of crystalline orientation can be improved with an increase of draw ratio and thus results in a high modulus and strength for the resulting POM fiber samples. In addition, the thermal analysis indicates that the crystallinity of the as-spun fibers can be enhanced by post-drawing due to the orientation-induced crystallization.

Optimization of melt-spinning parameters of poly(ethylene terephthalate) partially oriented multi-filament yarn in an industrial scale: Central composite design approach

Central Composite Design and Response Surface Methodology for Optimizing the Diameter of Electrospun Polyamide-6,6 Nanofiber Mat

Statistical modeling of polyester filament yarn evenness with respect to some melt spinning parameters

Optimization of the Production Process of Flash-Spinning UHMWPE Superfine Fiber by Response Surface Methodology

Preparation, mechanical properties and microstructure of polyoxymethylene fiber through melt spinning and hot drawing by using injection-molding grade resins

Evaluation of the effective parameters on the electrospinning of polyvinyl alcohol–chitosan nanofibers using response surface methodology (RSM)

Process optimization of electrospun polycaprolactone and nanohydroxyapatite composite nanofibers using response surface methodology

Optimization Of High-Density Polyethylene Process Based On Molecular Weight Distribution And Chemical Composition Distribution Under Uncertainty

Optimization of hot drawing process of ultra‐high molecular weight polyethylene monofilament prepared by melt spinning

Inspecting Process-Diameter Relationships of Forcespun PVP Ultrafine Fibers via RSM and ANN-PCA Approaches

Development of sustainable dual core-spun yarns using several filaments and recycled cotton sourced from pre-consumer fabric waste

Correlations between molecular weight, mechanical properties and morphology of micro-injection molded polyoxymethylene (POM)

Optimization of the Electrospun Niobium–Tungsten Oxide Nanofibers Diameter Using Response Surface Methodology

Optimization of Electrospinning Parameters for Lower Molecular Weight Polymers: A Case Study on Polyvinylpyrrolidone

Melt electrospinning process optimization of polylactic acid nanofibers

The Optimization of Process Parameters and Characterization of High-Performance CF/PEEK Composites Prepared by Flexible CF/PEEK Plain Weave Fabrics

Tuning drafting zone parameters for polyester yarn within a ring spinning system: modeling and optimization

Numerical Study of Melt-Spinning Dynamic Parameters and Microstructure Development with Ongoing Crystallization

Optimisation of cationic dye dyeing process of Porel fabrics using response surface methodology

Determination of Optimal Process Parameters for Plastic Injection Molding of Polymer Materials Using Multi-Objective Optimization

Response Surface Methodology to Explore the Influence Mechanism of Fiber Diameter in a New Multi-Needle Electrospinning Spinneret